Research of heat history analysis of industrial metal product using positron gamma spectroscopy

工业金属制品正电子伽马能谱热史分析研究

• 批准号: 20560050
• 负责人: KUROKI Kenro
• 金额: $ 2.91万
• 依托单位: National Research Institute of Police Science
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2008
• 资助国家: 日本
• 起止时间: 2008 至 2010
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-20560050/
• 关键词: 陽電子; 消滅ガンマ線; 金属材料; 熱履歴

The heat history analysis of a metallic material and the production process analysis of the thin metallic film were examined by the positron annihilation gamma rays simultaneous energy measurement method. When the influence of the oxide film was able to be excluded, the heat-treatment history of the metal was able to be detected. The possibility of the measurement of the film thickness was shown and the possibility of the distinction of the production process between vapor-deposited film and the plating film was also shown for the of the thin metallic film.

采用正电子湮灭伽马射线同步能量测量法对金属材料的热程分析和金属薄膜的生产过程进行了分析。当能够排除氧化膜的影响时，就能够检测到金属的热处理历史。指出了薄膜厚度测量的可能性，并对金属薄膜的制备提出了气相沉积膜和电镀膜的生产工艺区别的可能性。

项目成果

陽電子分光による材質分析

使用正电子光谱进行材料分析

• 发表时间: 2010
• 作者: 藤川健一;実吉敬二;黒木健郎
• 通讯作者: 黒木健郎

陽電子分光法による熱履歴分析-銅板における酸化膜の影響

使用正电子能谱进行热历史分析 - 铜板上氧化膜的影响

• 发表时间: 2008
• 作者: 黒木健郎;黒沢健至;土屋兼一;黒木健郎
• 通讯作者: 黒木健郎