Multi-scale evaluation of joint part based on local material testing

基于局部材料测试的接头零件多尺度评价

• 批准号: 20560085
• 负责人: OGAWA Takeshi
• 金额: $ 3万
• 依托单位: Aoyama Gakuin University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2008
• 资助国家: 日本
• 起止时间: 2008 至 2010
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-20560085/
• 关键词: マイクロ材料力学; 構造・機能材料; 材料強度; 信頼性評価; 接合技術

Indentation method is applied to materials testing for welding part, joint part of electronic components and thin film materials. These tests can reveals the residual stress and the effect of microstructures on mechanical properties of electronic joint part, and static strength, fatigue strength and anisotropic mechanical properties of thin films. Furthermore, the indentation method is applied to evaluate time-dependent characteristics of high-polymer materials. The results show that the indentation method can evaluate the master curve of viscoelastic characteristics.

压痕法适用于电子元件的焊接件、接头件和薄膜材料的材料检测。这些试验可以揭示电子接头零件的残余应力和微观组织对力学性能的影响，以及薄膜的静强度、疲劳强度和各向异性力学性能。此外，还将压痕法应用于评价高分子材料的时变特性。结果表明，压痕法可以评价粘弹性特性的主曲线。

项目成果

インデンテーション法による高分子材料のクリープコンプライアンスの測定

压痕法测量聚合物材料的蠕变柔量

• 发表时间: 2008
• 作者: 岡崎信平;坂上賢一;伊藤史;小川武史
• 通讯作者: 小川武史

インデンテーション法による粘弾性特性の評価と時間-温度換算則の適用

压痕法评价粘弹性及时间-温度转换规则的应用

• 发表时间: 2008
• 期刊: 日本機械学会論文集(A)編 75巻
• 作者: 坂上賢一;岡崎信平;小川武史
• 通讯作者: 小川武史

インデンテーション法によるWC-Co溶射材の静的および疲労強度特性評価

压痕法评价WC-Co热喷涂材料的静态和疲劳强度特性

• 发表时间: 2010
• 期刊: 日本機械学会論文集A編
• 作者: 中西公紀;坂上賢一;小川武史;小林圭史
• 通讯作者: 小林圭史

インデンテーション法による局所力学特性評価および微視組織解析

使用压痕法进行局部力学性能评估和微观结构分析

• 发表时间: 2008
• 作者: 小川武史;坂上賢一
• 通讯作者: 坂上賢一

インデンテーション法による粘弾性特性のマスター曲線評価

使用压痕法评估粘弹性的主曲线

• 发表时间: 2010
• 作者: 坂上賢一;小川武史
• 通讯作者: 小川武史