Preparation and application of anisotropy proton-conducting membranes with micro-phase structure

微相结构各向异性质子导膜的制备及应用

• 批准号: 20560664
• 负责人: ASANO Masaharu
• 金额: $ 2.66万
• 依托单位: Japan Atomic Energy Agency
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2008
• 资助国家: 日本
• 起止时间: 2008 至 2010
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-20560664/
• 关键词: 燃料電池電解質膜; イオン照射; 光グラフト重合; 燃料電池用電解質膜; イオンビーム照射

To develop a polymer electrolyte membrane with high proton conductivity in the thickness direction of the membrane, a ETFE film was first irradiated with swift heavy ions to form the cylindrical damage zone (the so-called latent track region), followed by UV-grafting of styrene into the latent tracks and subsequent sulfonation. The UV-grafting was found to occur only in the latent tracks. As a result, the proton conductivity of the resulted membrane was quite higher in the thickness direction than that in the surface direction.

为了开发在膜厚度方向上具有高质子传导率的聚合物电解质膜，首先用快重离子照射ETFE膜以形成圆柱形损伤区（所谓的潜迹区），然后将苯乙烯紫外接枝到潜迹中并随后磺化。发现紫外线接枝仅发生在潜在轨道中。结果，所得膜的厚度方向的质子电导率比表面方向的质子电导率高得多。

项目成果

光グラフト重合によるフッ素系ポリマー電解質膜の開発

光接枝聚合含氟聚合物电解质膜的开发

• 发表时间: 2008
• 作者: 浅野雅春;陳進華;前川康成;吉田勝
• 通讯作者: 吉田勝

HDPE基材に基づく固体高分子型燃料電池膜-UV法とγ法の比較-

基于HDPE基材的固体聚合物燃料电池膜-UV法与γ法的比较-

• 发表时间: 2008
• 作者: 浅野雅春;陳進華;前川康成;吉田勝;浅野雅春;木村祥亮,山本利徳,黒田真一,片貝良一,久保田仁,陳進華,浅野雅春,前川康成,吉田勝;木村祥亮(浅野雅春)
• 通讯作者: 木村祥亮(浅野雅春)

HDPE基材に基づく固体高分子型燃料電池-UV法とγ法の比較-

基于HDPE基材的固体聚合物燃料电池-UV法与γ法的比较-

• 发表时间: 2008
• 作者: 浅野雅春;陳進華;前川康成;吉田勝;浅野雅春;木村祥亮,山本利徳,黒田真一,片貝良一,久保田仁,陳進華,浅野雅春,前川康成,吉田勝
• 通讯作者: 木村祥亮,山本利徳,黒田真一,片貝良一,久保田仁,陳進華,浅野雅春,前川康成,吉田勝

光グラフト重合を利用したフッ素系高分子電解質膜の開発

利用光接枝聚合技术开发含氟聚合物电解质膜

• 发表时间: 2008
• 期刊: 膜(MEMBRANE) 33(2)
• 作者: 浅野雅春;陳進華;前川康成;吉田勝
• 通讯作者: 吉田勝

ホームページ等。

主页等