Basic research on oxidation resistance of heat-resisting alloys in water vapor

耐热合金在水蒸气中抗氧化性能的基础研究

• 批准号: 20560679
• 负责人: AMANO Tadaaki
• 金额: $ 2.75万
• 依托单位: Shonan Institute of Technology
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2008
• 资助国家: 日本
• 起止时间: 2008 至 2010
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-20560679/
• 关键词: 水蒸気酸化; 耐熱合金; アルミナ; 白金; イットリウム; スケールの密着性; スケールの微細構造; サイクル酸化; 高温酸化

In order to clarify the oxidation resistance of heat-resisting alloys in water vapor, rare earth and noble metal were added to alumina-forming alloy. The oxide adherence of the alloy with 0.5mass% platinum addition was markedly improved. The oxide adherence of the alloy with 0.5mass% yttrium addition was also improved even cyclic oxidation. It is suggested that the addition promotes a keying effect via Y3Al5O12 oxide pegs at the oxide/alloy interface.

为了阐明耐热合金在水蒸气中的抗氧化性能，在氧化铝成形合金中添加了稀土和贵金属。添加0.5质量%铂后，合金的氧化附着力明显提高。添加0.5%Y的合金的氧化附着力也得到改善，甚至循环氧化。结果表明，Y3Al5O12的加入通过Y3Al5O12氧化物在氧化物/合金界面的钉扎作用促进了键合效应。

项目成果

Reactive Element Addition for Cr_2O_3- and Al_2O_3-Forming Heat-Resisting Alloys

Cr_2O_3和Al_2O_3耐热合金的反应元素添加

• 发表时间: 2011
• 作者: 安田清和;T.Amano
• 通讯作者: T.Amano

微量のイットリウムを添加したアルミナ生成合金の酸素-水蒸気雰囲気におけるサイクル酸化

含微量钇的氧化铝形成合金在氧气-蒸汽气氛中的循环氧化

• 发表时间: 2010
• 作者: 阿部雄太

Scale Surface and Scale/Alloy Interface for Alumina- and Chromia-Forming Alloys with Noble Metals and Rare Earths

含贵金属和稀土的氧化铝和氧化铬形成合金的氧化皮表面和氧化皮/合金界面

• 发表时间: 2010
• 作者: 阿部雄太;天野忠昭
• 通讯作者: 天野忠昭

High-Temperature Oxidation Resistance of Al_2O_3-Forming Heat-Resisting Alloys with Noble Metals and Rare Earth, European Federation of Corrosion Workshop

贵金属和稀土组成的Al_2O_3耐热合金的高温抗氧化性，欧洲腐蚀联合会联合会

• 发表时间: 2009
• 作者: Yoshihisa Uchida;Niichi Hayashi;JiaSheng Ru;Xin Wang;Hideo Furuhashi;Yoshiyuki Uchida;Akihiro Kono;Gerard Touchard;天野忠昭
• 通讯作者: 天野忠昭

希土類元素添加によるクロミア生成耐熱合金の高温酸化挙動

添加稀土元素的氧化铬耐热合金的高温氧化行为

• 发表时间: 2009
• 作者: 浅井零;他;天野忠昭
• 通讯作者: 天野忠昭