Polymerization shrinkage mechanism, using micro-CT for tracing filler movement in light cured resin composite.

聚合收缩机制，使用微型 CT 追踪光固化树脂复合材料中填料的运动。

• 批准号: 20791383
• 负责人: CHOU Eitetsu
• 金额: $ 2.25万
• 依托单位: Tokyo Medical and Dental University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2008
• 资助国家: 日本
• 起止时间: 2008 至 2010
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-20791383/
• 关键词: 光重合型コンポジットレジン; 重合収縮; マイクロX線CT; マイクロフォーカスX線CT

The aim of this study was to evaluate the shrinkage vectors of light-cured composites during polymerization in a deep class I cavity. Experimental resin composite was filled into a box-shaped class I cavity with or without a bonding agent. The polymerization shrinkage vectors depend on both depth and conversion degree. The application of micro-CT is a novel approach to present an overall profile and quantitatively measure shrinkage of dental composites.

本研究的目的是评估光固化复合材料在聚合过程中的收缩矢量在一个深I类腔。实验树脂复合材料填充到盒形I类腔中，有或没有粘合剂。聚合收缩矢量取决于深度和转化度。显微CT的应用是一种新的方法来呈现整体轮廓和定量测量牙科复合材料的收缩。

项目成果

Real-time Tomographic Monitoring of Composite Restoration Placement Using SS-OCT

使用 SS-OCT 实时断层扫描监测复合修复体的放置

• 发表时间: 2010
• 作者: 高橋加奈子;他;A.SADR
• 通讯作者: A.SADR

Regional shrinkage vectors of light-cured composites by micro-CT filler tracing

通过微型 CT 填料追踪得到光固化复合材料的区域收缩矢量

• 发表时间: 2010
• 作者: 坂田篤信、吉嶺嘉人、松本妃可;他;Eitetsu Cho
• 通讯作者: Eitetsu Cho

Evaluation of resin composite polymerization by three dimensional micro-CT imaging and nanoindentation

• DOI: 10.1016/j.dental.2011.07.008
• 发表时间: 2011-11-01
• 期刊: DENTAL MATERIALS
• 影响因子: 5
• 作者: Cho, Eitetsu;Sadr, Alireza;Tagami, Junji
• 通讯作者: Tagami, Junji

Real-Time Gap Formation of Resin Composites Using SS-OCT during Photo polymerization

在光聚合过程中使用 SS-OCT 实时形成树脂复合材料的间隙

• 发表时间: 2010
• 作者: Jiro Miura;Noriaki Hasegawa;J.R.MAYORAL
• 通讯作者: J.R.MAYORAL

マイクロCTを使ったコンポジットレジンの重合収縮挙動の観察

利用显微CT观察复合树脂的聚合收缩行为

• 发表时间: 2010
• 作者: 藤井慎介;前田英史;友清淳;橋口勇;門野内聡;堀清美;和田尚久;赤峰昭文;趙永哲
• 通讯作者: 趙永哲