Improvement of Corrosion Resistance of Magnesium Alloys by Controlling of Microstructure and Electrochemical Homogeneity

通过控制微观结构和电化学均匀性提高镁合金的耐腐蚀性能

• 批准号: 20686050
• 负责人: YAMASAKI Michiaki
• 金额: $ 16.72万
• 依托单位: Kumamoto University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (A)
• 财政年份: 2008
• 资助国家: 日本
• 起止时间: 2008 至 2010
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-20686050/
• 关键词: マグネシウム; 加工熱処理; 急速凝固; 組織制御; 腐食防食; 長周期積層構造

Highly corrosion-resistant Mg-Zn-rare earth (RE) alloys with long period stacking ordered phase have been developed by microstructure control through the rapid solidification and thermo-mechanical treatment. Enhancement of microstructural and electrochemical homogeneities in the Mg-Zn-RE alloys by rapid solidification techniques results in the passivity of substrate materials.

采用快速凝固和形变热处理相结合的方法，通过对Mg-Zn-RE合金组织的控制，制备了具有长周期堆垛有序相的高耐蚀Mg-Zn-RE合金。通过快速凝固技术提高Mg-Zn-RE合金的组织和电化学均匀性，导致基体材料的钝化。

项目成果

Influence of Fourth Element Addition on Corrosion Property of Mg-Zn-Gd Alloys with LPSO phase

第四元素添加对LPSO相Mg-Zn-Gd合金腐蚀性能的影响

• 发表时间: 2010
• 作者: T. Oyama;T. Okajima;T. Ohsaka;S. Yamaguchi;N. Oyama;M.Otani
• 通讯作者: M.Otani

Multimodal Microstructure Evolution and Mechanical Properties of Extruded Mg-Zn-Gd Alloys with Long-period Stacking Ordered Phase

长周期堆垛有序相挤压Mg-Zn-Gd合金的多峰显微组织演化和力学性能

• 发表时间: 2009
• 作者: H. Habara;他;山崎倫昭
• 通讯作者: 山崎倫昭

高強度高靭性金属及びその製造方法

高强度、高韧性金属及其制造方法

• 发表时间: 2008

Mg-Zn-Y基押出合金の塑性挙動の温度依存性, 組織形態が及ぼす寄与

Mg-Zn-Y 基挤压合金塑性行为的温度依赖性、微观结构的贡献

• 发表时间: 2008
• 作者: Mohamed S.El-Deab;Takeo Ohsaka;B.E.El-Anadouli;木下昭人
• 通讯作者: 木下昭人

Effect of Extrusion Parameters on Mechanical Properties of Mg97Zn1Y2 Alloys at Room and Elevated Temperatures

• DOI: 10.2320/matertrans.maw201026
• 发表时间: 2010-09-01
• 期刊: MATERIALS TRANSACTIONS
• 影响因子: 1.2
• 作者: Hirano, Masaaki;Yamasaki, Michiaki;Kawamura, Yoshihito
• 通讯作者: Kawamura, Yoshihito