Ultrathin proton conductive membrane based on polymer nanosheetassembly

基于聚合物纳米片组装的超薄质子传导膜

• 批准号: 20750083
• 负责人: MATSUI Jun
• 金额: $ 2万
• 依托单位: Tohoku University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2008
• 资助国家: 日本
• 起止时间: 2008 至 2009
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-20750083/
• 关键词: 機能性高分子; プロトン伝導膜; 高分子ナノシート; スルホン酸誘導体; Langmuir-Blodgett膜

We prepared ultrathin proton conductive membrane based on polymer nanosheet assembly. The polymer nanosheet was prepared by acryamide-based copolymer, which contains sulfonic acid as a proton conductive group. The polymer nanosheet showed the proton conductivity of 10^<-6> S/cm at room temp, RH=100%. Moreover, the conductivity of 10^<-2> S/cm was achieved using acid-based type polymer nanosheet assembly.

采用聚合物纳米片组装法制备了纳米级质子传导膜。以磺酸为质子传导基团的丙烯酰胺基共聚物为原料制备了聚合物纳米片。聚合物纳米片<-6>在室温、RH= 100%下显示出10 μ S/cm的质子传导率。此外，<-2>使用酸基型聚合物纳米片组装体实现了10 μ S/cm的电导率。

项目成果

イミダゾール基を有するポリマーの合成と Langmuir-Blodgett 膜形成能の検討

含咪唑基聚合物的合成及Langmuir-Blodgett成膜能力研究

• 发表时间: 2009
• 作者: 工藤倫子;松井淳;宮下徳治
• 通讯作者: 宮下徳治

プロトン伝導部位を有する高分子ナノシートの作製

具有质子传导位点的聚合物纳米片的制备

• 发表时间: 2008
• 作者: S.Toyoda;H.Takahashi;H Kumigashira;M.Oshima;et al.;F. Miyamaru;N.K. Das;工藤倫子
• 通讯作者: 工藤倫子

界面場を用いたナノ材料のボトムアップ集積と機能発現

使用界面场的纳米材料自下而上的集成和功能表达

• 发表时间: 2009
• 作者: S.S.A.Rahman;D.Kawaguchi;Y.Matsushita;松井淳
• 通讯作者: 松井淳

シリル基を含む高分子ナノシートの作製と超薄膜レジストへの応用

含硅烷基聚合物纳米片的制备及其在超薄膜抗蚀剂中的应用

• 发表时间: 2008
• 作者: Y. Shinzato;et. al.;Sabiha Sultana
• 通讯作者: Sabiha Sultana

Solid-State Electrochemical Transistor Based onπ-Conjugated Polymer Langmuir-Blodgett Film

基于π共轭聚合物Langmuir-Blodgett薄膜的固态电化学晶体管

• 发表时间: 2010
• 期刊: Jpn. J. Appl. phys. 49
• 作者: J. Matsui;M. Yamakoshi;T. Miyashita
• 通讯作者: T. Miyashita