Diffusion behavior of interstitials in platinum-metal-group metals

铂族金属中间隙原子的扩散行为

• 批准号: 20760477
• 负责人: SEKIDO Nobuaki
• 金额: $ 2.16万
• 依托单位: National Institute for Materials Science
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2008
• 资助国家: 日本
• 起止时间: 2008 至 2009
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-20760477/
• 关键词: 高温材料; 拡散; 金属物性; 表面処理; 界面構造; 格子欠陥; 元素戦略; 白金族金属

This project has focused on designing an effective coating system against carbon based high temperature structural materials. Platinum group metals were chosen as candidates for a diffusion barrier that prevents carbon outward and oxygen inward diffusion. Their applicability was examined on the basis of carbon diffusion behavior. Pt is found to possess quite low carbon diffusivity, suggesting that Pt is promising for this type of application.

本项目致力于设计一种针对碳基高温结构材料的有效涂层体系。铂族金属被选为防止碳向外扩散和氧向内扩散的扩散屏障。根据碳扩散行为考察了它们的适用性。发现铂具有相当低的碳扩散系数，这表明铂在这类应用中很有前途。

项目成果

Growth behavior and interfacial character of Ir3Y precipitates in the Ir2Y Lave phase matrix

Ir3Y 沉淀物在 Ir2Y Lave 相基体中的生长行为和界面特征

• 发表时间: 2010
• 期刊: Mater. Trans. 51
• 作者: N. Sekido;Y. Yamabe-Mitarai
• 通讯作者: Y. Yamabe-Mitarai

Development of porous ceramics layers through sublimation of metallic phases

通过金属相升华开发多孔陶瓷层

• 发表时间: 2009
• 期刊: International Journal of Refractory Metals and Hard Materials 27
• 作者: N. Sekido;Y. Yamabe-Mitarai
• 通讯作者: Y. Yamabe-Mitarai

Ir_2Y母相中におけるIr_3Y相の析出とその成長挙動

Ir_2Y基体中Ir_3Y相的析出及其生长行为

• 发表时间: 2009
• 作者: Hideaki Takahashi;Masatoshi Sakairi;Tatsuya Kikuchi;介川裕章;関戸 信彰
• 通讯作者: 関戸 信彰

多孔質セラミックとその製造方法

多孔陶瓷及其制造方法

• 发表时间: 2008

Laves相Ir_2YにおけるIr_3Yの析出挙動

Laves相Ir_2Y中Ir_3Y的析出行为

• 发表时间: 2008
• 作者: 黒田大介;小野嘉則;御手洗容子;香河英史;後藤大亮;菊地竜也;関戸 信彰