Establishment of New Hybrid Surface Modification Including DLC Coatings as Final Treatment

建立新的混合表面改性，包括 DLC 涂层作为最终处理

• 批准号: 21560090
• 负责人: MORITA Tatsuro
• 金额: $ 3.16万
• 依托单位: Kyoto Institute of Technology
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2009
• 资助国家: 日本
• 起止时间: 2009 至 2011
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-21560090/
• 关键词: DLC被覆; 複合表面改質; 耐摩耗性; 疲労

This study was conducted to establish a new process of hybrid surface modification which can contribute for improving performance and efficiency of mechanical products. The process was composed of various DLC coatings(Me-DLC, multi-layered DLC) and pre-treatments. The objective materials were a titanium alloy and stainless steel possessing poor wear resistance but fine functionalities together. This study accumulated systematic results concerning the effects of the DLC coatings and pre-treatments on the friction-wear properties, mechanical properties and fatigue properties.

本研究旨在建立一种新的复合表面改性工艺，以提高机械产品的性能和效率。该工艺由各种DLC涂层（Me-DLC，多层DLC）和预处理组成。目标材料是耐磨性差但功能良好的钛合金和不锈钢。本研究系统地研究了类金刚石膜及预处理对摩擦磨损性能、力学性能和疲劳性能的影响。

项目成果

プラズマ窒化およびSi-DLC被覆処理を施したステンレス鋼の摩擦特性および疲労特性

等离子渗氮和Si-DLC涂层处理不锈钢的摩擦和疲劳性能

• 发表时间: 2010
• 作者: 安達晃一;森田辰郎;廣田悟史;池永勝;加賀谷忠治
• 通讯作者: 加賀谷忠治

表面改質材の疲労強度の考え方と最近の研究

表面改性材料疲劳强度的概念和最新研究

• 发表时间: 2009
• 期刊: 金属
• 作者: 森田辰郎;加賀谷忠治
• 通讯作者: 加賀谷忠治

表面改質および組織制御によるチタンの高性能化

通过表面改性和结构控制提高钛的性能

• 发表时间: 2012
• 期刊: チタン
• 作者: Y-H. Huang;S-T. Tu;F-Z. Xuan and T. Itoh;森田辰郎
• 通讯作者: 森田辰郎

DLC被覆処理と金属材料の疲労強度の関係

DLC涂层处理与金属材料疲劳强度的关系

• 发表时间: 2011
• 作者: 坂井田喜久;森田辰郎;柿内利文;坂井田喜久;森田辰郎
• 通讯作者: 森田辰郎

表面改質および組織制御によるチタン合金の高性能化

通过表面改性和微观结构控制提高钛合金的性能

• 发表时间: 2011
• 作者: 相賀裕太郎;長谷部忠司;山下翔平;森田辰郎
• 通讯作者: 森田辰郎