The next-generation lead acid battery using a composite of nano-particles from hydrolysis and a conductive polymer

使用水解纳米颗粒和导电聚合物复合材料的下一代铅酸电池

• 批准号: 21560768
• 负责人: TAGUCHI Masami
• 金额: $ 3万
• 依托单位: Akita University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2009
• 资助国家: 日本
• 起止时间: 2009 至 2011
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-21560768/
• 关键词: 各種製造プロセス; 鉛蓄電池; 二酸化鉛; ナノ粒子; 二次電池; 導電性ポリマー; コンポジット電極

A series of PbO_2 nanoparticles prepared by hydrolysis of lead acetate in various mixtures of water and alcohol were characterized, and the properties of the novel lead acid battery using the nanoparticles as the active materials for positive electrode were examined by discharge-charge cycling. All the nanoparticles, which were identified as β-PbO_2 single phase, ranged from about 9 to 13 nm in diameter. In comparison with the PbO_2 powder prepared by the conventional method in lead acid battery industry, namely the electrolytic oxidation of lead powder, the PbO_2 nanoparticles had remarkably high performance in both utilization of the active materials for positive electrode and the current efficiency during discharge-charge cycling

采用不同的水和乙醇混合溶液对一系列醋酸铅纳米粒子进行了表征，并通过放电-充电循环测试了以该纳米粒子为正极活性物质的新型铅酸电池的性能。所有纳米颗粒均为β-PbO2单相，直径在9~13 nm之间。与铅酸蓄电池工业中的传统方法即铅粉的电解氧化相比，纳米PbO_2在正极活性物质的利用率和充放电循环中的电流效率方面都具有显著的高性能

项目成果

化学工業日報,2009/3/25掲載,鉛バッテリー正極利用率2.2倍に,高容量鉛蓄電池

发表于化工日报2009年3月25日铅蓄电池正极使用率提高2.2倍高容量铅酸蓄电池

鉛蓄電池正極, 鉛蓄電池および鉛蓄電池用正極の製造法

铅酸电池正极、铅酸电池及其制造方法

• 发表时间: 2010

水素還元されたPt Oxide Blackのメタノール酸化特性

氢还原氧化铂黑的甲醇氧化性能

• 发表时间: 2012
• 期刊: J. MMIJ
• 作者: 田口正美;川端泰弘;小坂勇樹
• 通讯作者: 小坂勇樹

ナノスケールPbO_2を用いた鉛蓄電池正極活物質の充放電特性

纳米PbO_2铅酸电池正极活性材料的充放电特性

• 发表时间: 2011
• 作者: 佐々木利裕;田口正美
• 通讯作者: 田口正美

Methanol Oxidation Activities of Pt Oxide Thin Films Prepared by Reactive Sputtering

反应溅射制备氧化铂薄膜的甲醇氧化活性

• 发表时间: 2010
• 期刊: Int. J. Soc. Mater. Eng. Resor
• 作者: M. Taguchi;J. Nakayama;K. Itou;N. Nagai
• 通讯作者: N. Nagai