Formation of β'phase in a β Ti alloy and Widmanstatten structure in a Ti-Al alloy

β Ti 合金中 β 相的形成和 Ti-Al 合金中魏氏组织的形成

• 批准号: 21760559
• 负责人: SAKAMOTO Tatsuaki
• 金额: $ 2.75万
• 依托单位: Ehime University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2009
• 资助国家: 日本
• 起止时间: 2009 至 2010
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-21760559/
• 关键词: チタン合金; 時効析出; 相分解; 透過型電子顕微鏡; オメガ相; 相分離; ラメラ組織; 表面起伏; β型チタン合金; チタン-アルミニウム合金; 二相分離; ウィドマンシュテッテン組織

As for β-type Ti-6.8Mo-4.5Fe-1.5Al(mass%)alloy, a new path of phase transformation was found. Two-step aging gives rise to precipitation of β' phase which does not precipitate during single-step aging. This result is important for controlling microstructure in β-type Ti alloys. As for Ti-48.5at%Al, crystallographic data of Widmanstatten structure, such as habit plane and volume fraction of constituent phases, were obtained. These results are important for clarifying mechanism of formation of Widmanstatten structure.

对于β型Ti-6.8Mo-4.5Fe-1.5Al（质量分数）合金，发现了一条新的相变途径：两步时效导致β'相析出，而单步时效则没有β'相析出。这一结果对控制β型钛合金的显微组织具有重要意义。对于Ti-48.5at%Al合金，获得了魏氏组织的晶习面和组成相的体积分数等晶体学数据。这些结果对阐明魏氏组织的形成机理具有重要意义。

项目成果

Ti-48.5at%Alに生成したウィドマンシュテッテン組織の微細組織解析

Ti-48.5at%Al 中形成的魏德曼组织的微观结构分析

• 发表时间: 2009
• 作者: 阪本辰顕;福留裕太(学部生);仲井清眞;小林千悟
• 通讯作者: 小林千悟

Ti-48.5 at% Al合金におけるウィドマンシュテッテン組織形成過程

Ti-48.5 at% 铝合金魏德曼组织形成过程

• 发表时间: 2010
• 作者: 多根正和;中嶋英雄;中野貴由;新家光雄;倉本繁;Tatsuaki Sakamoto;阪本辰顕;阪本辰顕
• 通讯作者: 阪本辰顕

Ti-6.8Mo-4.5Fe-1.5Alにおけるβ'相の析出

Ti-6.8Mo-4.5Fe-1.5Al 中β相的析出

• 发表时间: 2009
• 作者: 阪本辰顕;福留裕太(学部生);仲井清眞;小林千悟;Ryusuke Nakamura;酒道武浩;阪本辰顕;阪本辰顕;阪本辰顕
• 通讯作者: 阪本辰顕

Ti-6.8Mo-4.5Fe-1.5Alにおける2段時効に伴う相分離

Ti-6.8Mo-4.5Fe-1.5Al 中两阶段时效导致的相分离

• 发表时间: 2010
• 作者: 多根正和;中嶋英雄;中野貴由;新家光雄;倉本繁;Tatsuaki Sakamoto;阪本辰顕
• 通讯作者: 阪本辰顕

Ti-6.8Mo-4.5Fe-1.5Alの機械的性質に及ぼす2段時効の効果

两阶段时效对Ti-6.8Mo-4.5Fe-1.5Al力学性能的影响

• 发表时间: 2009
• 作者: 多根正和;中嶋英雄;中野貴由;新家光雄;倉本繁;Tatsuaki Sakamoto;阪本辰顕;阪本辰顕;桧垣侑里
• 通讯作者: 桧垣侑里