A development of a new durability test using dentin adhesive systems and an analysis of mechanisms of adhesive degradation.

使用牙本质粘合剂系统开发新的耐久性测试并分析粘合剂降解机制。

• 批准号: 21791851
• 负责人: NAKATA Takashi
• 金额: $ 3万
• 依托单位: Okayama University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2009
• 资助国家: 日本
• 起止时间: 2009 至 2010
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-21791851/
• 关键词: Tooth Wear; 保存修復学; Toot Wear

Results of this study revealed that a new thermal cycling method was useful to evaluate the durability of dentin adhesive systems. Moreover, either MMP inhibitors or mineral oil suppressed gradually bond strength reductions of dentin adhesions. It could thus be suggested that the degradation of dentin adhesion was due to degrade collagen fibrils in dentin matrix caused by endogenous MMPs.

本研究结果表明，一种新的热循环方法可用于评估牙本质粘接剂系统的耐久性。此外，无论是MMP抑制剂还是矿物油，都能逐渐抑制牙本质粘连的结合强度降低。可见，内源性MMPs降解牙本质基质中的胶原原纤维是导致牙本质粘附降解的主要原因。

项目成果

MMAレジンセメントのサーマルサイクリング後および水中浸漬後の象牙質接着強さ

热循环和水中浸泡后MMA树脂水门汀的牙本质粘合强度

• 发表时间: 2010
• 期刊: 接着歯学 Vol.28
• 作者: 中田貴;西谷佳浩;吉山昌宏
• 通讯作者: 吉山昌宏

物性の異なる修復材料のサーマルサイクリング後の象牙質接着強さ

不同物理性质的修复材料热循环后牙本质结合强度

• 发表时间: 2010
• 作者: 中田貴;李相紅;西谷佳浩;吉山昌宏;中田貴;中田貴
• 通讯作者: 中田貴

浸漬溶液の違いがサーマルサイクル負荷後の象牙質接着強さに及ぼす影響

不同浸泡液对热循环加载后牙本质粘结强度的影响

• 发表时间: 2010
• 作者: 中田貴;李相紅;西谷佳浩;吉山昌宏;中田貴;中田貴;中田貴;中田貴
• 通讯作者: 中田貴

MMA系レジンセメントのサーマルサイクリング後および水中浸漬後の象牙質接着強さ

热循环和水中浸泡后MMA树脂水门汀的牙本质粘合强度

• 发表时间: 2010
• 期刊: 接着歯学
• 作者: 中田貴;西谷佳浩;吉山昌宏;中田貴
• 通讯作者: 中田貴

次亜塩素酸ナトリウム処理した象牙質へのMMA系レジンセメント3種の接着強さ

三种MMA树脂水门汀与次氯酸钠处理牙本质的粘附强度

• 发表时间: 2009
• 期刊: 接着歯学 Vol.27
• 作者: 中田貴;李相紅;西谷佳浩;吉山昌宏
• 通讯作者: 吉山昌宏