Development of Cathode Catalysts with High Durability for Polymer Electrolyte Fuel Cells Using Pseudocapacitance of Metal Oxides

利用金属氧化物赝电容开发聚合物电解质燃料电池高耐久性阴极催化剂

• 批准号: 22560693
• 负责人: NOHARA Shinji
• 金额: $ 2.91万
• 依托单位: University of Yamanashi
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2010
• 资助国家: 日本
• 起止时间: 2010 至 2012
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-22560693/
• 关键词: 固体高分子形燃料電池; 金属酸化物; 擬似容量; カソード触媒; カーボン劣化; 酸化スズ; 起動停止

Addition of Nb-SnO2 prepared by flame combustion method resulted in suppression of a rise in the potential of electrodes with commercial Pt/GCB (graphitized carbon black)catalysts. In the simulated startup/shutdown cycling of membrane electrode assembly (MEA), it was found that addition of the Nb-SnO2 suppressed decay in the electrochemical active area (ECA) during the test. S tructural and compositional analyses of MEAs after the test strongly suggested that it should be due to suppression of degradation of carbon in the catalyst layer.

通过火焰燃烧法制备的Nb-SnO 2的添加导致抑制与商业Pt/GCB（石墨化炭黑）催化剂的电极的电位的上升。在膜电极组件（MEA）的模拟启动/关闭循环中，发现添加Nb-SnO 2抑制了测试期间电化学活性区域（ECA）的衰减。测试后MEA的结构和组成分析强烈表明，这应该是由于抑制了催化剂层中碳的降解。

项目成果

SiO_2高分散ポリイミド系電解質膜の作製と特性評価

SiO_2高分散聚酰亚胺电解质膜的制备及性能评价

• 发表时间: 2010
• 作者: 山下裕己;野原愼士;内田誠;内田裕之;渡辺政廣;山下 裕己;野原愼士
• 通讯作者: 野原愼士

疑似容量を有する酸化スズの添加による固体高分子形燃料電池用カソード触媒の高耐久化

添加赝容量氧化锡提高聚合物电解质燃料电池阴极催化剂的耐久性

• 发表时间: 2012
• 作者: 山下裕己;野原愼士;内田誠;内田裕之;渡辺政廣
• 通讯作者: 渡辺政廣