Developing dental implant titanium alloys with antibacterial property

开发具有抗菌性能的种植牙钛合金

• 批准号: 22791921
• 负责人: TAKAHASHI Masatoshi
• 金额: $ 2.58万
• 依托单位: Tohoku University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2010
• 资助国家: 日本
• 起止时间: 2010 至 2011
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-22791921/
• 关键词: チタン合金; 歯科用合金; インプラント; バイオフィルム; 生体適合性; 耐食性; 歯科補綴物; チタン銀合金

Aiming to develop dental implant titanium alloys with antibacterial property, we prepared experimental Ti-Ag alloys and investigated their properties. The Ti-Ag alloys showed good corrosion resistance in a NaCl solution and a lactic acid solution. The Ti-Ag alloys had excellent tarnish resistance in a NaCl solution, a lactic acid solution, a Na_2S solution and a povidone iodine solution. Their resistance was comparable to that of pure titanium.

为了开发具有抗菌特性的牙齿植入物合金，我们准备了实验性Ti-Ag合金并研究了它们的性质。 Ti-Ag合金在NaCl溶液和乳酸溶液中表现出良好的耐腐蚀性。 TI-AG合金在NaCl溶液，乳酸溶液，Na_2s溶液和Povidone碘溶液中具有出色的粉状耐药性。它们的抵抗力与纯钛相当。

项目成果

The development of binary titanium alloys with the aim of dental applications

以牙科应用为目标的二元钛合金的开发

• 发表时间: 2011
• 作者: Yukyo Takada;Masatoshi Takahashi;Masafumi Kikuchi
• 通讯作者: Masafumi Kikuchi

Ti-Ag合金の0. 1%硫化ナトリウム水溶液中における耐変色性

Ti-Ag合金在0.1%硫化钠水溶液中的耐变色性能

• 发表时间: 2011
• 作者: Yukyo Takada;Masatoshi Takahashi;Masafumi Kikuchi;高橋正敏
• 通讯作者: 高橋正敏

Ti-Ag合金の0.1%硫化ナトリウム水溶液中における耐変色性

Ti-Ag合金在0.1%硫化钠水溶液中的耐变色性能

• 发表时间: 2011
• 作者: Yukyo Takada;Masatoshi Takahashi;Masafumi Kikuchi;高橋正敏;高橋正敏
• 通讯作者: 高橋正敏

Corrosion resistance of dental Ti-Ag alloys in NaCl solution

牙科钛银合金在氯化钠溶液中的耐腐蚀性能

• 发表时间: 2010
• 期刊: Materials Transactions Vol.51
• 作者: Takahashi M;Kikuchi M;Takada Y;Okuno O
• 通讯作者: Okuno O

擬似体液中における試作Ti-Ag合金表面へのリン酸カルシウム自然形成

模拟体液中原型钛银合金表面自然形成磷酸钙

• 发表时间: 2009
• 作者: Takahashi M;Kikuchi M;Hatori K;Orii Y;Sasaki K;Takada Y;高橋正敏;高橋正敏;Masatoshi TAKAHASHI;Masatoshi TAKAHASHI;高橋正敏;高橋正敏;Takahashi M;高橋正敏;高橋正敏
• 通讯作者: 高橋正敏