Analysis of molecular orientation of cyclo-olefin copolymer film during sequential-biaxial stretching.

环烯烃共聚物薄膜在顺序双轴拉伸过程中的分子取向分析。

• 批准号: 22750200
• 负责人: TAKARADA Wataru
• 金额: $ 2.58万
• 依托单位: Tokyo Institute of Technology
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2010
• 资助国家: 日本
• 起止时间: 2010 至 2011
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-22750200/
• 关键词: 高分子; 繊維加工; フィルム; 延伸; 分子配向; 非晶高分子; 2軸延伸

In-situ stress and birefringence measurements were performed during the stretching and relaxation processes of cyclo-olefine copolymer films. When the measurement was conducted at a high temperature, stress-birefringence behavior corresponds to two phase model with rubber part and glass part. However, when the measurement was conducted at temperatures close to glass transition temperature and at high strain rates, existence of the 3rd component which has negative birefringence and medium level of relaxation time was founded.

在环链共聚物膜的拉伸和松弛过程中，进行了原位应力和双折射测量。当测量在高温下进行测量时，应力屈光行为对应于带有橡胶部分和玻璃部分的两个相模型。但是，当在接近玻璃过渡温度的温度下进行测量并以高应变速率进行测量时，建立了第三个成分的存在，该组件的存在为负双向，并建立了中等水平的松弛时间。

项目成果

Stress versus Birefringence Behavior during Uniaxial Stretching and Relaxation Processes of Cyclo-olefin Copolymer Films

环烯烃共聚物薄膜单轴拉伸和松弛过程中的应力与双折射行为

• 发表时间: 2011
• 作者: H. Menju;W. Takarada;T. Kikutani
• 通讯作者: T. Kikutani

環状オレフィンコポリマーのガラス転移点近傍での伸長挙動の温度・歪速度依存性

环烯烃共聚物玻璃化转变点附近伸长行为的温度和应变速率依赖性

• 发表时间: 2010
• 作者: X. Meng;K. Fujita;S. Murai;J. Konishi;M. Mano;and K. Tanaka;毛受広人
• 通讯作者: 毛受広人

On-line measurement of birefringence development during stretching of cycloolefin copolymer films

环烯烃共聚物薄膜拉伸过程中双折射发展的在线测量

• 发表时间: 2010
• 作者: K.Ikeda;H.Menju;W.Takarada;T.Kikutani
• 通讯作者: T.Kikutani

環状オレフィン共重合体の伸張過程における応力-複屈折挙動の温度・歪速度依存性

环烯烃共聚物拉伸过程中应力双折射行为的温度和应变速率依赖性

• 发表时间: 2011
• 作者: 毛受広人;宝田亘;鞠谷雄士
• 通讯作者: 鞠谷雄士

繊維と工業:複屈折の測定法と解析事例

纺织和工业：双折射测量方法和分析实例

• 发表时间: 2010
• 作者: 鞠谷雄士,宝田亘;他
• 通讯作者: 他