Development of a novel radiation-induced grafting technique using ultraviolet light irradiation

利用紫外线照射开发新型辐射诱导嫁接技术

• 批准号: 22760584
• 负责人: TAKADA Tomoya
• 金额: $ 2.58万
• 依托单位: Asahikawa National College of Technology
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2010
• 资助国家: 日本
• 起止时间: 2010 至 2012
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-22760584/
• 关键词: 高分子成形加工操作; 放射線グラフト重合; 紫外線照射; 異性化反応; グラフト技術; 放射線; 紫外線

The effect of ultraviolet (UV) light illumination on the yield of radiation-induced graft polymerization onto polypropylene was examined. The yield observed for the polymer irradiated successively with X-ray and UV was found to be higher than that observed for the polymer irradiated only with X-ray. The author proposed a mechanism of the yield improvement caused by UV illumination on the basis of the present and previous studies; the improvement is caused by thephoto-induced isomerization of hydrocarbon polymer radicals.

研究了紫外光照射对聚丙烯辐射接枝聚合产率的影响。X射线和紫外线连续照射的聚合物的产额比只用X射线照射的聚合物的产额要高。作者在前人研究的基础上，提出了紫外光提高产率的机理，认为提高产率的原因是烃类聚合物自由基光诱导异构化。

项目成果

ポリプロピレンへの放射線グラフト生成に対する紫外線照射効果

紫外线照射对聚丙烯辐射接枝形成的影响

• 发表时间: 2013
• 作者: 高田知哉;小泉均
• 通讯作者: 小泉均

ポリプロピレンへの放射線グラフト重合に対する紫外線照射効果

紫外线照射对聚丙烯辐射接枝聚合的影响

• 发表时间: 2013
• 作者: 高田知哉;小泉均
• 通讯作者: 小泉均