Design of a process producing joint materials by using surface porous gradient structure

利用表面多孔梯度结构生产接头材料的工艺设计

• 批准号: 22656173
• 负责人: TANAKA Toshihiro
• 金额: $ 2.26万
• 依托单位: Osaka University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Challenging Exploratory Research
• 财政年份: 2010
• 资助国家: 日本
• 起止时间: 2010 至 2011
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-22656173/
• 关键词: 酸化還元; 表面微細孔; 水熱反応; 表面傾斜孔径分布; Cu

We found a new procedure to make a surface porous structure by oxidation and reduction processes for a metal substrate. If the distribution of pore size has gradient from the bulk to the surface of the substrate, we can penetrate glass or ceramics into those pores and solidify them to make a new joint material which has high joint strength because of mutual penetration of two phases. Finally, we found some adequate experimental conditions to make the above porous surface structure.

我们发现了一个新的程序，使表面多孔结构的氧化和还原过程的金属基板。如果孔隙尺寸分布从基体到表面呈梯度分布，则可以将玻璃或陶瓷渗透到这些孔隙中，并使其固化，制成一种新型的连接材料，由于两相的相互渗透，具有高的连接强度。最后，我们找到了一些适当的实验条件，使上述多孔表面结构。

项目成果

水熱反応-マイクロ加熱プロセスを用いた銀微粒子担持多孔質ガラスの作製

水热反应-微加热法制备载银颗粒多孔玻璃

• 发表时间: 2011
• 期刊: 日本金属学会
• 作者: 吉川健;笠松敬;金田貴文;平井信充;田中敏宏;森浩亮
• 通讯作者: 森浩亮

Nano-Porous Layer on Steel Surface as Lubricant Carrier

钢表面纳米多孔层作为润滑剂载体

• 发表时间: 2011
• 期刊: J. Nanosci. Nanotechnol
• 作者: Hiroshi Utsunomiya;Shogo Kawajiri;Nobuyuki Takahira;Tetsuo Sakai;and Toshihiro Tanaka
• 通讯作者: and Toshihiro Tanaka

水熱反応を利用したスラグ含有ガラスからの発泡材料作製の試み

尝试利用水热反应从含渣玻璃制造泡沫材料

• 发表时间: 2012
• 作者: 〓田宗一郎;鈴木賢紀;田中敏宏
• 通讯作者: 田中敏宏

低環境負荷微細孔材料作製の試みマクロおよびミクロポーラス金属の開発最前線

尝试创造对环境影响低的微孔材料 宏观和微孔金属发展的最前沿

• 发表时间: 2011
• 作者: 田中敏宏;鈴木賢紀;平井信充
• 通讯作者: 平井信充

高温界面物性とその応用

高温界面性能及其应用

• 发表时间: 2012
• 作者: 〓田宗一郎;鈴木賢紀;田中敏宏;田中敏宏
• 通讯作者: 田中敏宏