The development of small diameter artificial vessels consisted with PVA hydrogel

PVA水凝胶小直径人工血管的研制

• 批准号: 22659322
• 负责人: TAHARA Shinya
• 金额: $ 2.11万
• 依托单位: Kobe University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Challenging Exploratory Research
• 财政年份: 2010
• 资助国家: 日本
• 起止时间: 2010 至 2011
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-22659322/
• 关键词: 再生医学; 人工血管; ポリビニルアルコール; 再生医療

The small diameter(3mm) conduit consisted with PVA hydrogel was transplanted to rat abdominal artery. Immediately after the transplantation, beating was observed, however, all conduits were occulted in a few days. Next, endothelial cells were co-cultured with PVA sheet. No endothelial cells were adhered to PVA sheet. The collagen fragment was embedded into PVA hydrogel and endothelial cells were co-cultured with rotation. These cells were, then, adhered and migrated. In addition, smooth muscle cells were co-cultures, and these cells also adhered to the collagen-PVA sheet.

将PVA水凝胶制成的小直径（3 mm）导管移植于大鼠腹主动脉。移植后立即观察到搏动，然而，所有导管在几天内被闭塞。接着，将内皮细胞与PVA片共培养。没有内皮细胞粘附到PVA片材。将胶原片段包埋于PVA水凝胶中，旋转培养内皮细胞。然后，这些细胞粘附并迁移。此外，平滑肌细胞是共培养的，并且这些细胞也粘附到胶原-PVA片上。

项目成果

A Simplest Method of Flap Monitoring

• DOI: 10.1055/s-0030-1251562
• 发表时间: 2010-09-01
• 期刊: JOURNAL OF RECONSTRUCTIVE MICROSURGERY
• 影响因子: 2.1
• 作者: Sakakibara, Shunsuke;Hashikawa, Kazunobu;Tahara, Shinya
• 通讯作者: Tahara, Shinya

脱細胞化組織を用いた小口径人工血管の開発とその評価

使用脱细胞组织的小直径人造血管的开发和评估

• 发表时间: 2011
• 作者: Sakakibara S;Hashikawa K;Omori M;Terashi H;Tahara S.;榊原俊介
• 通讯作者: 榊原俊介

高張塩溶液脱細胞化法による脱細胞化血管の開発とその評価

高渗盐溶液脱细胞法脱细胞血管的开发与评价

• 发表时间: 2010
• 作者: Sakakibara S;Hashikawa K;Omori M;Terashi H;Tahara S.;榊原俊介;榊原俊介;榊原俊介;榊原俊介;榊原俊介
• 通讯作者: 榊原俊介

0. 5mm径PVAハイドロゲル製血管モデルを用いるスーパーマイクロサージャリーのトレーニング

0.使用直径5mm的PVA水凝胶血管模型进行超级显微外科训练

• 发表时间: 2010
• 作者: 須永中;菅原康志;宇田宏一;去川俊二;桂木容子;宮崎邦夫;加持秀明;橋川和信
• 通讯作者: 橋川和信

0.5mm径PVAハイドロゲル製血管モデルを用いるスーパーマイクロサージャリーのトレーニング

使用0.5毫米直径PVA水凝胶血管模型进行超级显微外科训练

• 发表时间: 2010
• 作者: 須永中;菅原康志;宇田宏一;去川俊二;宮崎邦夫;今西理也;加持秀明;橋川和信
• 通讯作者: 橋川和信