Investigation on complex deterioration of chloride attack and ASR followed by a repair method using lithium salt

研究氯化物侵蚀和 ASR 的复杂恶化以及使用锂盐的修复方法

• 批准号: 23360197
• 负责人: UEDA Takao
• 金额: $ 11.07万
• 依托单位: The University of Tokushima
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (B)
• 财政年份: 2011
• 资助国家: 日本
• 起止时间: 2011-04-01 至 2014-03-31
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-23360197/
• 关键词: 塩害; ASR; 複合劣化; リチウム塩; 電気化学的手法

The complex deterioration mechanism of chloride attack and ASR was intensively affected by the environmental temperature, and in the case of the alkali supply from outside of concrete, the penetration of Cl- was suppressed by the progress of ASR around the surface layer of concrete.Moreover, as a repair method against such a complex deterioration mechanism, an electrochemical technique using an electrolyte solution containing the lithium nitrate among various kinds of lithium salt. Especially, when the environmental temperature was 40 degrees Celsius, the penetration of Li+ was promoted remarkably and the expansion of concrete after the treatment was suppressed.

环境温度对Cl-侵蚀和ASR的复杂劣化机制影响较大，在混凝土外供碱情况下，混凝土表层周围ASR的进展抑制了Cl-的渗透。此外，作为一种针对这种复杂劣化机制的修复方法，在各种锂盐中使用含有硝酸锂的电解质溶液的电化学技术。特别是当环境温度为40℃时，显著促进了Li+的渗透，抑制了处理后混凝土的膨胀。

项目成果

塩害とASRの複合劣化に対する電気化学的補修工法の検討

盐害与ASR复合劣化电化学修复方法研究

• 发表时间: 2013
• 作者: 七澤 章;櫛田淳二;上田隆雄;塚越雅幸
• 通讯作者: 塚越雅幸

各種リチウム塩によるASR抑制効果に関する検討

各种锂盐抑制ASR效果的研究

• 发表时间: 2011
• 作者: 上田隆雄;新田建也;松本義章;七澤章
• 通讯作者: 七澤章

温度変化が塩害とASRの複合劣化機構に与える影響

温度变化对盐害与ASR联合劣化机制的影响

• 发表时间: 2011
• 期刊: コンクリート構造物の補修・補強・アップグレード論文報告集
• 作者: 上田隆雄;他
• 通讯作者: 他

塩害とＡＳＲの複合劣化に対する電気化学的補修工法の検討

盐害与ASR复合劣化电化学修复方法研究

• 发表时间: 2013
• 作者: 七澤 章;櫛田淳二;上田隆雄;塚越雅幸
• 通讯作者: 塚越雅幸

塩害とASRの複合劣化機構と電気化学的補修に関する検討

盐害与ASR联合劣化机理及电化学修复研究

• 发表时间: 2012
• 期刊: コンクリート工学年次論文集
• 作者: 櫛田淳二;上田隆雄;塚越雅幸;七澤 章
• 通讯作者: 七澤 章