Research on the visualization of injection process in complex shaped molding and the suppression technology of polymer degradation

复杂形状成型注射过程可视化及聚合物降解抑制技术研究

• 批准号: 23560146
• 负责人: FUKUSHIMA YOSHIO
• 金额: $ 3.33万
• 依托单位: Gunma Prefectural Industrial Technology Center
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2011
• 资助国家: 日本
• 起止时间: 2011 至 2013
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-23560146/
• 关键词: 射出成形; 分解ガス; ガス焼け不良; ガス収集; 可視化; モニタリング

Various approaches to solve the problem of molding defects like the warpage, the short-shot, and the burn marks have been investigated. In order to observe transition phenomena in the polymer injection, determination of outgas composition and visualization of inside situation in injection process were carried out in this work. In addition, rationalized gas monitoring method by utilizing sensor device was also examined to realize real time monitoring at the actual shot. It was successfully obtained that key chemical reactions in regard with appearance of burn mark by taking consideration into conditions which influenced the composition change of outgas. Finally basic knowledge to suppress molding defects was also discussed.

各种方法来解决成型缺陷的问题，如翘曲，短射，和烧伤的痕迹已被调查。为了观察聚合物注入过程中的过渡现象，进行了聚合物注入过程出气成分测定和内部情况可视化研究。此外，还探讨了利用传感器装置进行合理化瓦斯监测的方法，实现了在实际炮点的真实的实时监测。通过考虑影响排气成分变化的条件，成功地得到了与烧痕出现有关的关键化学反应。最后讨论了抑制成型缺陷的基本知识。

项目成果

不活性ガス雰囲気下での金属界面におけるPBTのガス焼け現象

惰性气体气氛下PBT在金属界面处的气体燃烧现象

• 发表时间: 2014
• 作者: 鈴木崇;福島祥夫;黒岩広樹;恩田絋樹;小松秀和 他
• 通讯作者: 小松秀和 他

型技術

模具技术

• 发表时间: 2013
• 作者: 福島祥夫;黒岩広樹;小松秀和;鈴木崇 他;T. ONO;高岡登志仁,福島祥夫,須田高史
• 通讯作者: 高岡登志仁,福島祥夫,須田高史

実成形時の燃焼ガス収集とガス組成分析によるPBT燃焼挙動に関する研究

通过实际成型过程中燃烧气体收集和气体成分分析研究PBT燃烧行为

• 发表时间: 2014
• 期刊: 成形加工
• 作者: 福島祥夫;黒岩広樹;小松秀和;鈴木崇 他
• 通讯作者: 鈴木崇 他

ガスセンサによる実成形時の発生ガス検知に関する基礎的検討

气体传感器检测实际成型过程中产生的气体的基础研究

• 作者: 福田眞;乳井剛晃;福島祥夫 鈴木崇 黒岩広樹 小松秀和
• 通讯作者: 福島祥夫 鈴木崇 黒岩広樹 小松秀和

成形不良を監視する装置付き金型

具有成型缺陷监控装置的模具

• 发表时间: 2012