The study of new composition glass electrode for ozone generation

新型臭氧发生玻璃电极的研究

• 批准号: 23560883
• 负责人: SOUNAI Atsuo
• 金额: $ 3.41万
• 依托单位: Suzuka National College of Technology
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2011
• 资助国家: 日本
• 起止时间: 2011 至 2013
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-23560883/
• 关键词: 電極触媒; バリヤー放電; オゾン; ホウケイ酸ガラス

currently, barrier discharge is widely used for the ozone generation,and its reactor has the dielectric electrode such as lead glass, which was prohibited on rohs regulation, so new lead free glass was tried to develop and the composition glass of sio2/b2o3/ na2o or k2o was investigated and it was found that k2o rich glass generated 1.1g/m3 ozone, nearly equal to max ozone of lead glass.further, new composition of borate silicate glass contained alkali earth element was developed and it showed excellent ozone generation performance and the higher generation rate than the current glass materials.

目前，阻挡放电被广泛用于臭氧产生，其反应器具有RoHS法规禁止的铅玻璃等介质电极，因此试图开发新的无铅玻璃，并研究了SiO_2/B_2O_3/Na_2O或K_2O组成的玻璃，发现富K_2O玻璃产生1.1g/m~3的臭氧，几乎相当于铅玻璃的最大臭氧。此外，还开发了含有碱土元素的新型硼硅酸盐玻璃，它具有良好的臭氧产生性能，并且比现有玻璃材料的臭氧产生速率更高。

项目成果

バリヤー放電によるオゾン発生に及ぼす非鉛電極材料の研究

无铅电极材料对阻挡放电产生臭氧的影响研究

• 发表时间: 2014
• 作者: 坂井 亮介;宗内 篤夫
• 通讯作者: 宗内 篤夫

バリヤー放電に及ぼす非鉛ガラス電極材料の研究

无铅玻璃电极材料对阻挡放电影响的研究

• 发表时间: 2013
• 作者: 宗内篤夫;坂井亮介
• 通讯作者: 坂井亮介

前田光彦バリヤー放電における非鉛ガラス電極材料の研究

前田光彦阻挡放电无铅玻璃电极材料研究

• 发表时间: 2012
• 作者: 前田光彦;宗内 篤夫;宗内篤夫
• 通讯作者: 宗内篤夫

バリヤー放電における非鉛ガラス電極の研究

阻挡放电无铅玻璃电极的研究

• 发表时间: 2013
• 作者: 宗内 篤夫; 坂井 亮介
• 通讯作者: 坂井 亮介

バリヤー放電におけるガラス電極の研究

玻璃电极阻挡放电研究

• 发表时间: 2013
• 作者: 前田光彦;宗内 篤夫
• 通讯作者: 宗内 篤夫