Development of nano-structured super-lattice hybrid material for highly qualified optical modulation device

开发用于高品质光调制器件的纳米结构超晶格混合材料

• 批准号: 23651088
• 负责人: OGAWA Tomoyuki
• 金额: $ 2.58万
• 依托单位: Tohoku University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Challenging Exploratory Research
• 财政年份: 2011
• 资助国家: 日本
• 起止时间: 2011 至 2012
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-23651088/
• 关键词: ナノ粒子; 超格子; 自己組織化

Synthesis of Au core/iron-oxide shell hybrid nanoparticles and fabrication of their self-assembled nanoparticle film have been developed to investigate optical modification of spectra through surface plasmon effect. We successfully synthesized Au core nanoparticle with 6nm in diameter covered by iron-oxide shell with 1.8~2.9nm in thickness. And we could observed the maximum absorption of the spectrum for the hybrid nanoparticle film at 580nm due to surface plasmon resonance, which was unchanged with that of the hybrid nanoparticle dispersion solution although showed a red-shift from that of Au nanoparticle dispersion solution. From this result, the surface plasmon resonance is very sensitive to dielectric constant of adjacent material to Au surface.

本文研究了金核/氧化铁壳杂化纳米粒子的合成及其自组装纳米粒子膜的制备，并利用表面等离子体效应对光谱进行了光学修饰。我们成功地合成了直径为6nm的金核纳米粒子，并覆盖了厚度为1.8~2.9nm的氧化铁壳。由于表面等离子体共振，杂化纳米颗粒膜在580nm处的光谱吸收最大，与杂化纳米颗粒分散溶液的光谱吸收没有变化，但与金纳米颗粒分散溶液的光谱吸收有红移。由此可见，表面等离子体共振对相邻材料的介电常数非常敏感。

项目成果

Spin-glasslike behavior of magnetic ordered state originating from strong interparticle magnetostatic interaction in α-Fe nanoparticle agglomerate

• DOI: 10.1063/1.3602313
• 发表时间: 2011-06-20
• 期刊: APPLIED PHYSICS LETTERS
• 影响因子: 4
• 作者: Hiroi, Kosuke;Kura, Hiroaki;Sato, Tetsuya
• 通讯作者: Sato, Tetsuya

Coulomb blockade phenomenon in ultra-thin gold nanowires

• DOI: 10.1063/1.3689844
• 发表时间: 2012-03-01
• 期刊: JOURNAL OF APPLIED PHYSICS
• 影响因子: 3.2
• 作者: Guerin, Hoel;Yoshihira, Masanori;Maki, Hideyuki
• 通讯作者: Maki, Hideyuki

強い磁気双極子相互作用を有する強磁性ナノ粒子集合体が示す粒子間磁化配列の磁気イメージング観察

具有强磁偶极相互作用的铁磁纳米颗粒聚集体表现出的颗粒间磁化排列的磁成像观察

• 发表时间: 2013
• 作者: K. Hiroi;H. Kura;T. Ogawa;M. Takahashi and T. Sato;神林宏明,廣井孝介,藏裕彰,小川智之,高橋研,佐藤徹哉
• 通讯作者: 神林宏明,廣井孝介,藏裕彰,小川智之,高橋研,佐藤徹哉

Current Perspective on Low Temperature...

当前对低温的看法...

• 发表时间: 2011
• 作者: K. Hiroi;H. Kura;T. Ogawa;M. Takahashi and T. Sato;神林宏明,廣井孝介,藏裕彰,小川智之,高橋研,佐藤徹哉;廣井孝介,藏裕彰,小川智之,高橋研,佐藤徹哉;廣井孝介,藏裕彰,小川智之,高橋研,佐藤徹哉;T. Ogawa
• 通讯作者: T. Ogawa

強い粒子間磁気双極子相互作用を有する薄膜状粒子集合体の磁性II

具有强颗粒间磁偶极相互作用的薄膜状颗粒聚集体的磁性II

• 发表时间: 2013
• 作者: K. Hiroi;H. Kura;T. Ogawa;M. Takahashi and T. Sato;神林宏明,廣井孝介,藏裕彰,小川智之,高橋研,佐藤徹哉;廣井孝介,藏裕彰,小川智之,高橋研,佐藤徹哉
• 通讯作者: 廣井孝介,藏裕彰,小川智之,高橋研,佐藤徹哉