Protonation of oxides using charge transfer reaction

利用电荷转移反应进行氧化物质子化

• 批准号: 23655201
• 负责人: MATSUMOTO Hiroshige
• 金额: $ 2.66万
• 依托单位: Kyushu University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Challenging Exploratory Research
• 财政年份: 2011
• 资助国家: 日本
• 起止时间: 2011 至 无数据
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-23655201/
• 关键词: レドックスプロトン化; プロトン伝導性酸化物; 酸素空孔; 水和; 両極性拡散

A new method of protonating oxides, via change in oxidation state of transition metal dopant was examined to create a brand new proton conducting oxides that possibly operate at intermediate-low temperatures. Experimental results suggested protonation taking place in Mn-doped SrZrO_3 and Mn-doped LaYbO_3. It is elucidated that the present method of protonation can work for oxides. On the other hand, LaYbO_3 has been found as a high protonic conductor even of transition metal was not introduced to be further investigated.

研究了一种通过改变过渡金属掺杂剂的氧化态来质子化氧化物的新方法，以创造一种可能在中低温下工作的全新质子传导氧化物。实验结果表明Mn掺杂SrZrO_3和Mn掺杂LaYbO_3中发生质子化。研究表明，本发明的质子化方法适用于氧化物。另一方面，即使没有引入过渡金属，LaYbO_3也被发现是一种高质子导体，有待进一步研究。

项目成果

SrZr1-xMnxo3-dにおけるレドックス型プロトネーション

SrZr1-xMnxo3-d 中的氧化还原质子化

• 发表时间: 2011
• 作者: 小材剛史;佐藤恭彦;酒井孝明;奥山勇治;松本広重
• 通讯作者: 松本広重

LaYbO3系酸化物におけるドーパント種が与えるプロトン導電特性への影響

掺杂剂种类对 LaYbO3 基氧化物质子传导性能的影响

• 发表时间: 2012
• 作者: R. Takabe;K. O. Hara;M. Baba;W. Du;N. Shimada;K. Toko;N. Usami;and T. Suemasu;鈴木義和;奥山勇治,小材剛史,酒井孝明,松本広重
• 通讯作者: 奥山勇治,小材剛史,酒井孝明,松本広重

SrZr1-xMnxO3-δにおけるレドックス型プロトネーション

SrZr1-xMnxO3-δ 中的氧化还原质子化

• 发表时间: 2011
• 作者: Toshiro Kogure;Kazuya Morimoto;Kenji Tamura;Hisako Sato and Akihiko Yamagishi;小材剛史,佐藤恭彦,酒井孝明,奥山勇治,松本広重
• 通讯作者: 小材剛史,佐藤恭彦,酒井孝明,奥山勇治,松本広重

La0. 9Sr0. 1Yb1-xInxO3-δペロブスカイト型酸化物のプロトン伝導特性

La0.9Sr0.1Yb1-xInxO3-δ钙钛矿氧化物的质子传导特性。

• 发表时间: 2012
• 作者: 愛須一史;鈴木 達;鈴木義和;池田翔平,奥山勇治,酒井孝明,松本広重
• 通讯作者: 池田翔平,奥山勇治,酒井孝明,松本広重

La0.9Sr0.1Yb1-xInxO3-δペロブスカイト型酸化物のプロトン伝導特性

La0.9Sr0.1Yb1-xInxO3-δ钙钛矿氧化物的质子传导性能

• 发表时间: 2012
• 作者: 池田翔平;奥山勇治;酒井孝明;松本広重
• 通讯作者: 松本広重