Attempt to Fabricate Metamaterials by Applying Nanohybrid Preparation

尝试通过应用纳米混合制备来制造超材料

• 批准号: 23655213
• 负责人: NORO Atsushi
• 金额: $ 2.66万
• 依托单位: Nagoya University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Challenging Exploratory Research
• 财政年份: 2011
• 资助国家: 日本
• 起止时间: 2011 至 2012
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-23655213/
• 关键词: ブロック共重合体; ナノ相分離構造; ミクロ相分離構造; 高圧重合; 可逆的付加開裂連鎖移動重合; ナノハイブリッド; 高分子量; ハイブリッド; メタマテリアル; 可逆付加開裂連鎖移動重合

Several attempts to fabricate metamaterials were made. Homogeneous nanohybrids were prepared by mixing a polystyrene-b-poly(vinylpyridine) block copolymer and hydroxy-capped semiconductor nanoparticles. Nanohybrids composed of a block copolymer and a metal salt were also prepared, and then nanoporous thin films were fabricated by removing the water soluble metal salt, which were remodified by another metal salt. Furthermore, high molecular weight block copolymers, which can be used as photonic films, were synthesized via reversible addition-fragmentation chain transfer polymerization under high pressure.

制造超材料进行了几次尝试。将聚苯乙烯-b-聚（乙烯吡啶）嵌段共聚物与羟基包覆半导体纳米粒子混合制备了均相纳米杂化体。制备了由嵌段共聚物和金属盐组成的纳米杂化体，然后通过去除水溶性金属盐制备纳米多孔薄膜，并用另一种金属盐对其进行改性。在高压下，采用可逆加成-破碎链转移聚合法制备了可用于光子薄膜的高分子量嵌段共聚物。

项目成果

ブロック共重合体のナノ相分離構造を鋳型としたハイブリッドの作製とそのモルフォロジー

以嵌段共聚物纳米相分离结构为模板制备杂化材料及其形貌

• 发表时间: 2011
• 作者: 野呂篤史;樋口康太;提嶋佳生;松下裕秀
• 通讯作者: 松下裕秀

名古屋大学 野呂篤史 助教

名古屋大学 野吕 敦 助理教授

超分子ポリマーゲル-分子デザインで構築するソフト材料-

超分子聚合物凝胶 - 采用分子设计构建的软质材料 -

• 发表时间: 2011
• 作者: Noro;Atsushi ; Yamagishi;Hajime ; Matsushita;Yushu;野呂篤史
• 通讯作者: 野呂篤史

ブロック共重合体/ 半導体ナノハイブリッドの調製とそのナノ相分離構造

嵌段共聚物/半导体纳米杂化物的制备及其纳米相分离结构

• 发表时间: 2011
• 作者: 樋口康太;提嶋佳生;野呂篤史;松下裕秀
• 通讯作者: 松下裕秀

Preparation of Block Copolymer/Metal Salt Hybrids and the Structural Isomer Effect of One Block on Their Morphologies

嵌段共聚物/金属盐杂化物的制备及其中一种嵌段的结构异构体对其形貌的影响

• 发表时间: 2011
• 作者: Yoshio Sageshima;Atsushi Noro;Yushu Matsushita
• 通讯作者: Yushu Matsushita