Development of concrete in cold region by using organic short fiber and ground granulated blast furnace slag

有机短纤维与磨细高炉矿渣研制寒区混凝土

• 批准号: 23760400
• 负责人: INOUE Masumi
• 金额: $ 2.5万
• 依托单位: Kitami Institute of Technology
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2011
• 资助国家: 日本
• 起止时间: 2011 至 2012
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-23760400/
• 关键词: コンクリート; 有機短繊維; 高炉スラグ微粉末; 耐凍害性; スケーリング; 気泡間隔係数; 有機繊維; 混和材; 寒冷地

The purpose of this study is to clarified the influence of organic short fiber and ground granulated blast furnace slag on frost damage resistance. Fleezing and thawing tests of concrete by using organic short fiber and ground granulated blast furnace slag were examined. In the case of fresh water, the influences of fiber content and ground granulated blast furnace slag on frost damage resistance of concrete appear relatively small. Within the range of replacement ratio used in this study, the frost damage resistance was remarkably high. On the other hand, the durability factor of concrete increases with the replacement of ground granulated blast furnace slag in the case of sea water, and the scaling of concrete decreases by using organic fiber in combination with ground granulated blast furnace slag. However, the scaling increases remarkably in the case of large replacement ratio of fiber.

本研究的目的是阐明有机短纤维和磨细的高炉矿渣对抗冻害性能的影响。研究了有机短纤维和磨细高炉矿渣对混凝土的软化和融化试验。在淡水条件下，纤维掺量和矿渣细粉对混凝土抗冻性的影响相对较小。在本研究使用的置换率范围内，抗冻性显著较高。另一方面，在海水中掺入磨细的高炉矿渣，混凝土的耐久系数增加，有机纤维与磨细的高炉矿渣复合使用，混凝土的结垢减少。当纤维取代率较大时，结垢显著增加。

项目成果

有機短繊維と高炉スラグ微粉末がコンクリートの耐凍害性に及ぼす影響

有机短纤维与粉化高炉矿渣对混凝土抗冻害性能的影响

• 发表时间: 2013
• 期刊: 土木学会北海道支部論文報告集
• 作者: 森将;井上真澄;岡田包儀
• 通讯作者: 岡田包儀

有機短繊維を用いたコンクリートの耐凍害性評価に関する基礎的研究

有机短纤维混凝土抗冻害评价基础研究

• 发表时间: 2012
• 期刊: 土木学会北海道支部論文報告集
• 作者: 森将;井上真澄;三上修一;猪狩平三郎;岡田包儀
• 通讯作者: 岡田包儀

有機短繊維および高炉スラグ微粉末がコンクリートの耐凍害性に及ぼす影響

有机短纤维与粉化高炉矿渣对混凝土抗冻害性能的影响

• 发表时间: 2012
• 作者: 森将;井上真澄;三上修一;岡田包儀
• 通讯作者: 岡田包儀