Creation of Surface Structures with High Corrosion Resistance forPt Catalyst of Fuel Cell

燃料电池Pt催化剂高耐腐蚀性表面结构的构建

• 批准号: 23760685
• 负责人: SUGAWARA Yu
• 金额: $ 2.75万
• 依托单位: Tohoku University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2011
• 资助国家: 日本
• 起止时间: 2011 至 2012
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-23760685/
• 关键词: 腐食防食; 電気化学; 白金; マイクロ電気化学セル; 白金単結晶; 白金触媒; 溶解

The influence of crystal orientation and grain boundary on the electrochemical property of Pt was studied to improve the durability of Pt catalyst in polymer electrolyte fuel cell. A microelectrochemical cell system enabled the electrochemical measurements on single planes in a polycrystalline Pt, and it was found that higher current densities by Pt oxidation was detected on the Pt(110) surface than Pt(100). Grain boundaries caused the increase of the oxidation current. This result implies the grain boundary is a predominant site of oxidation in a polycrystalline Pt.

为提高聚合物电解质燃料电池铂催化剂的耐久性，研究了晶向和晶界对铂电化学性能的影响。微电化学电池系统使得能够在多晶Pt中的单个平面上进行电化学测量，并且发现在Pt（110）表面上检测到的Pt氧化电流密度高于Pt（100）表面。晶界引起氧化电流的增加。这一结果意味着晶界是多晶Pt中氧化的主要部位。

项目成果

白金多結晶の電気化学特性に及ぼす面方位と粒界の影響

面取向和晶界对铂多晶电化学性能的影响

• 发表时间: 2013
• 作者: 佐々木麻由;菅原優;武藤泉;原信義
• 通讯作者: 原信義

白金の電気化学特性に及ぼす面方位と粒界の影響

面取向和晶界对铂电化学性能的影响

• 发表时间: 2013
• 作者: 佐々木麻由;菅原優;武藤泉;原信義
• 通讯作者: 原信義

マイクロ電気化学セルによる白金単一結晶面の電気化学特性の測定

使用微电化学电池测量铂单晶面的电化学性能

• 发表时间: 2012
• 作者: 佐々木麻由;菅原優;武藤泉;原信義
• 通讯作者: 原信義