Development of continuous precipitation process with crystal forms controlled by ionic strength

离子强度控制晶型的连续沉淀工艺的开发

• 批准号: 23656488
• 负责人: KAWASE Motoaki
• 金额: $ 2.5万
• 依托单位: Kyoto University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Challenging Exploratory Research
• 财政年份: 2011
• 资助国家: 日本
• 起止时间: 2011 至 2012
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-23656488/
• 关键词: 晶析; イオン強度; シュウ酸カルシウム; 結晶形; 不安定相; pH; 準安定相

Although fine particles are commonly produced by precipitation or crystallization in the industry , it is still difficult to predict and control the shape, size distribution, and crystal form of the resulting particles. In this study , continuous precipitation of calcium oxalate which exhibits pseudopolymorphism was carried out. Effects of pH and ion strength of the reactant solution were investigated quantitatively and attempted to control the crystal form. How the crystal form of calcium oxalate changes during crystal growth was found.

虽然工业上普遍采用沉淀法或结晶法生产细颗粒，但对生成颗粒的形状、粒度分布和晶体形态仍难以预测和控制。在本研究中，我们进行了草酸钙的连续沉淀，草酸钙呈现出伪多晶性。定量研究了反应物溶液的pH值和离子强度对晶型的影响，并尝试控制晶型。发现了草酸钙在晶体生长过程中的晶型变化。

项目成果

シュウ酸カルシウムの連続晶析におけるイオン強度の影響

离子强度对草酸钙连续结晶的影响

• 发表时间: 2012
• 作者: R. Tarumi;T. Matsuhisa and Y. Shibutani;岩井豊彦・河瀬元明
• 通讯作者: 岩井豊彦・河瀬元明

連続晶析における多形制御

连续结晶中的多晶型控制

• 发表时间: 2013
• 作者: Hiroyuki Komatsu;Masaki Ota;Masaru Watanabe;Yoshiyuki Sato;Richard L. Smith;Jr.;Hiroyuki Komatsu;早坂淳，大田昌樹，渡邉賢，Richard L. Smith Jr.;福田晃子・河瀬元明
• 通讯作者: 福田晃子・河瀬元明