海洋工程装备中的许多运动部件采用海水作为润滑介质，不仅节约资源，而且避免了润滑油的泄漏污染和易燃等弊端。然而，海水腐蚀性强、粘度低，润滑效果差，摩擦副材料存在腐蚀与磨损等问题，严重影响了运动部件的正常工作和使用寿命。设计开发适合海洋环境的新型摩擦副材料是亟待解决的重要课题。因此，本项目拟通过设计制备Fe基非晶/Si3N4复合涂层，利用Fe基非晶涂层耐腐蚀和耐磨损的特性，并发挥Si3N4对涂层的强韧化作用，以及Si3N4和海水发生摩擦反应生成硅胶膜发挥润滑作用的独特之处，赋予涂层海水中自润滑功能。研究Si3N4对涂层组织结构、硬度和韧性的影响，重点研究涂层在海水中的自润滑性能以及腐蚀与磨损交互行为，深入认识涂层在海水中摩擦失效时的动态演化机理。项目的实施不仅为海洋环境中服役的摩擦副材料提供了新的设计方法，也将为进一步探明摩擦副材料在海洋环境中的服役行为和腐蚀与磨损耦合作用规律提供理论依据。

Many moving parts used in marine engineering equipment use seawater as the lubricant to save oil resources and avoid its leakage and flammability. However, the friction pair lubricated by seawater is corroded and worn seriously because of the corrosion, low viscosity and poor lubrication characteristics of seawater, which affects the normal operation of the equipment seriously. Thus, it is very important to design and develop new friction materials suitable for marine environment. In this project, Fe based amorphous/Si3N4 composite coating will be prepared, Fe based amorphous coating as the corrosion and wear resistant substrate, Si3N4 not only plays the strengthening and toughening effect, but also gives the coating self-lubrication function in seawater by reacting with seawater to form silica gel film as lubricant during friction process. The effect of doping and content of Si3N4 on the structure, hardness and toughness, especially the self-lubrication, corrosion and wear interaction behavior of the coating in seawater will be studied, in order to understand the dynamic evolution of the failure mechanism of the coating in seawater. The successful implementation of this project will not only provides a new design method for friction materials in marine environment, but also provides law for exploring the service behavior and corrosion-wear coupling effect of friction materials in marine environment.