Preparation of soft magnetic FeCo-based films for writers
Preparation of soft magnetic FeCo-based films for writers
复制标题
书写用软磁FeCo基薄膜的制备
DOI：
10.1063/1.3078008
复制
发表时间：
2009-03
影响因子：
3.2
通讯作者：
Wei, Fulin
中科院分区：
文献类型：
--
作者：
Liu, Xiaoxi;Wang, Xuan;Wei, Dan;Zheng, Fu;Liu, Zhaoyang;Wei, Fulin
在FeCoAlO薄膜的射频溅射过程中，在环氧树脂中引入C元素，制备了新型软磁头材料FeCoAlOC纳米晶薄膜。当Al2O3与FeCo共溅射时，薄膜的软磁性能得到了很大的改善：矫顽力从几十个oersted降低到几个oersted （Hch ~ 4.8 Oe和Hce ~ 6.5 Oe）。随着碳的进一步添加，薄膜具有优异的软磁性能和良好的高频响应，矫顽力低至1.0 Oe，饱和Bs>20 kG, f≤1.0 GHz时磁导率μ ' >500，截止频率约为1.7 GHz。显微结构测试表明，薄膜的良好磁性能与薄膜的小增益尺寸有关。
New soft magnetic head materials, the nanocrystalline FeCoAlOC thin films, were prepared by introducing C element in epoxy resin during rf sputtering of FeCoAlO films. When Al2O3 was cosputtered with FeCo, soft magnetic properties of thin films were highly improved: the coercive force decreases from dozen of oersted to several oersted (Hch∼4.8 Oe and Hce∼6.5 Oe). With further addition of carbon, the thin films exhibit excellent soft magnetic properties and good high frequency response: the coercivity is as low as 1.0 Oe, with saturation Bs>20 kG, permeability μ′>500 when f≤1.0 GHz, and cutoff frequency around 1.7 GHz. The measurement of microstructure shows that the good magnetic properties are correlated with the small gain size of film.
登录
查看更多内容
影响因子：
3.2
作者：
H. Ono;M. Ishida;M. Fujinaga;H. Shishido;H. Inaba
通讯作者：
H. Ono;M. Ishida;M. Fujinaga;H. Shishido;H. Inaba
影响因子：
3.2
作者：
M. Pasquale;C. Sasso;A. Magni;F. Celegato;J. Sohn;S. Lim
通讯作者：
M. Pasquale;C. Sasso;A. Magni;F. Celegato;J. Sohn;S. Lim
DOI：
10.1016/s0921-5093(00)01753-6
发表时间：
2001-05
影响因子：
6.4
作者：
J. F. Löffler;H. Braun;W. Wagner;G. Kostorz;A. Wiedenmann
通讯作者：
J. F. Löffler;H. Braun;W. Wagner;G. Kostorz;A. Wiedenmann
影响因子：
64.8
作者：
Wang, SX;Sun, NX;Yabukami, S
通讯作者：
Yabukami, S
影响因子：
2.1
作者：
Yu Fu;T. Miyao;T. Yamakami;Zheng Yang;M. Matsumoto;Xiaoxi Liu;A. Morisako
通讯作者：
Yu Fu;T. Miyao;T. Yamakami;Zheng Yang;M. Matsumoto;Xiaoxi Liu;A. Morisako