Reduced Fracture Toughness of Metallic Glass at Cryogenic Temperature
Reduced Fracture Toughness of Metallic Glass at Cryogenic Temperature
复制标题
低温下金属玻璃断裂韧性降低
DOI：
10.3390/met7040151
复制
发表时间：
2017-04
期刊：
影响因子：
2.9
通讯作者：
Zhai Qijie
中科院分区：
文献类型：
--
作者：
Zhou Yihao;Liu Jiaxin;Han Dongxue;Chen Xiangru;Wang Gang;Zhai Qijie
研究了低温对锆基非晶合金韧性的影响。基于不同温度下的三维断口形貌，分析了裂纹的形成和扩展。通过对剪切转变区体积的计算，讨论了金属玻璃在不同温度下的剪切模量和体积模量以及与温度相关的裂纹形成机理。一旦裂纹开始扩展，超弹性模型被用来阐明裂纹扩展的断口演变。
The effects of cryogenic temperature on the toughness of a Zr-based metallic glass are investigated. Based on three-dimensional fracture morphologies at different temperatures, the crack formation and propagation are analyzed. Through the calculation of the shear transformation zone volume, the shear modulus and bulk modulus of the metallic glass at different temperatures and the crack formation mechanism associated with the temperature is discussed. Once the crack commences propagation, the hyperelasticity model is used to elucidate the fractographic evolution of crack propagation.
登录
查看更多内容
影响因子：
9.4
作者：
F. Jiang;M. Jiang;H. Wang;Yanglei Zhao;L. He;Jun Sun
通讯作者：
F. Jiang;M. Jiang;H. Wang;Yanglei Zhao;L. He;Jun Sun
影响因子：
9.4
作者：
B. Gludovatz;S. Naleway;R. Ritchie;J. Kruzic
通讯作者：
B. Gludovatz;S. Naleway;R. Ritchie;J. Kruzic
影响因子：
4.6
作者：
Wang YW;Bian XL;Wu SW;Hussain I;Jia YD;Yi J;Wang G
通讯作者：
Wang G
DOI：
10.1002/9781118801017.ch7.10
发表时间：
2021-02
期刊：
Encyclopedia of Glass Science, Technology, History, and Culture
影响因子：
--
作者：
D. V. Louzguine-Luzgin;A. Inoue
通讯作者：
D. V. Louzguine-Luzgin;A. Inoue
脆性大块金属玻璃中裂纹扩展的不稳定性
影响因子：
9.4
作者：
Wang, G.;Wang, W. H.;Chan, K. C.;Xu, X. H.
通讯作者：
Xu, X. H.