Cubic zinc hydroxide nitrate cavity and its lasing action
Cubic zinc hydroxide nitrate cavity and its lasing action
复制标题
立方氢氧化硝酸锌空腔及其激光作用
DOI：
10.1016/j.ijleo.2021.168472
复制
发表时间：
2021-12
期刊：
影响因子：
3.1
通讯作者：
Chunxiang Xu
中科院分区：
文献类型：
--
作者：
Xiuxiu Dong;Qiuxiang Zhu;Mingyue Zeng;Haiyun Lu;Xingyu Huang;Feng Chen;Chunxiang Xu
层状双氢氧化物(LDH)作为一种响应环境刺激的光致发光功能材料，近年来得到了推广和应用。本工作以氧化锌和硝酸锌溶液为原料，在常温下合成了一种羟基复盐--硝酸锌。为了进一步获得锌氢化物作为腔体的规整形貌，将上述锌氢化物在100℃下老化16h，利用微型光致发光光谱系统(μ-PL光谱系统)和325nm线的飞秒脉冲激光作为激发源，观察到了单个立方体锌氢化物腔体从放大的自发辐射到激光发射的有效转换。结果表明，立方体锌-HDS腔是一种理想的光电子器件微激光器材料。
Layered double hydroxide (LDH) has been promoted and applied as photoluminescent functional materials responding to environmental stimuli in recent years. In this work, a kind of hydroxy double salts, zinc hydroxide nitrate (Zn5(OH)8(NO3)2·2H2O, Zn-HDS) was fabricated from zinc oxide and zinc nitrate solution under ambient conditions. To further obtain the regular morphology of Zn-HDS as cavity, the aforementioned Zn-HDS was dehydrated by aging at 100 °C for 16 h. The effective conversion from amplified spontaneous emissions (ASE) into lasing emissions of a single cubic Zn-HDS cavity was observed with the help of micro-photoluminescence spectra system (μ-PL spectra system) and 325 nm line of a femtosecond pulsed laser as excitation source. The result indicated that the cubic Zn-HDS cavity can be applied as desirable microlaser material for optoelectronic devices.
登录
查看更多内容
影响因子：
9.9
作者：
A. Cursino;J. Gardolinski;F. Wypych
通讯作者：
A. Cursino;J. Gardolinski;F. Wypych
影响因子：
3.3
作者：
Hui Zhang;Kang-Yu Zou;Shaohua Guo;X. Duan
通讯作者：
Hui Zhang;Kang-Yu Zou;Shaohua Guo;X. Duan
DOI：
10.1002/chin.201450233
发表时间：
2014-12
期刊：
ChemInform
影响因子：
--
作者：
Guoli Fan;Feng Li;D. Evans;X. Duan
通讯作者：
Guoli Fan;Feng Li;D. Evans;X. Duan
影响因子：
3.3
作者：
A. Kaassis;Si-Min Xu;S. Guan;D. Evans;Min Wei;Gareth R. Williams
通讯作者：
A. Kaassis;Si-Min Xu;S. Guan;D. Evans;Min Wei;Gareth R. Williams
DOI：
10.1107/s0567740870003230
发表时间：
1970-01-01
期刊：
ACTA CRYSTALLOGRAPHICA SECTION B-STRUCTURAL CRYSTALLOGRAPHY AND CRYSTAL CHEMISTRY
影响因子：
--
作者：
STAHLIN, W;OSWALD, HR
通讯作者：
OSWALD, HR