Improved cytocompatibility of Mg-1Ca alloy modified by Zn ion implantation and deposition
Improved cytocompatibility of Mg-1Ca alloy modified by Zn ion implantation and deposition
复制标题
Zn离子注入和沉积改善Mg-1Ca合金的细胞相容性
DOI：
10.1016/j.matlet.2017.06.055
复制
发表时间：
2017-10
影响因子：
3
通讯作者：
Zheng Yufeng
中科院分区：
文献类型：
--
作者：
Liu Jiao;Zheng Yang;Bi Yanze;Li Yan;Zheng Yufeng
采用金属蒸气真空弧等离子体源（MEVVA）对Mg-1Ca合金进行了Zn离子注入和沉积（II&D）改性。研究了其表面特性、腐蚀行为和细胞相容性。俄歇电子能谱（AES）结果表明，Mg-1Ca合金表面形成了均匀的ZnO层。电化学测试结果表明，Zn改性后的Mg-1Ca合金在模拟体液（SBF）中的腐蚀电位有所提高，腐蚀电流密度也有较大幅度的提高。间接细胞活性评价和直接细胞培养结果表明，Mg-1Ca合金表面的ZnO层提高了MC 3 T3-E1细胞的细胞相容性。
The Mg-1Ca alloy has been modified by Zn ion implantation and deposition (II&D) using metal vapor vacuum arc plasma source (MEVVA). The surface characteristics, corrosion behavior and cytocompatibility were investigated. The auger electron spectroscopy (AES) results showed that a uniform ZnO layer was formed on the surface of Mg-1Ca alloy. The electrochemical measurements revealed that the corrosion potential has been increased, and a comparable corrosion current density in the simulated body fluid (SBF) was obtained for the Zn-modified Mg-1Ca alloy. The indirect cell viability evaluation and direct cell culture results indicated that the cytocompatibility of MC3T3-E1 cells on the Mg-1Ca alloy was improved by the ZnO layer on the surface.
登录
查看更多内容
影响因子：
6.7
作者：
Y. Wan;Guang-yao Xiong;Honglin Luo;F. He;Y. Huang;Y. L. Wang
通讯作者：
Y. Wan;Guang-yao Xiong;Honglin Luo;F. He;Y. Huang;Y. L. Wang
影响因子：
4.3
作者：
Yamaguchi, Masayoshi
通讯作者：
Yamaguchi, Masayoshi
影响因子：
3
作者：
Guosong Wu;L. Gong;K. Feng;Shuilin Wu;Ying Zhao;P. Chu
通讯作者：
Guosong Wu;L. Gong;K. Feng;Shuilin Wu;Ying Zhao;P. Chu
影响因子：
9.7
作者：
Zhao, Ying;Jamesh, Mohammed Ibrahim;Chu, Paul K.
通讯作者：
Chu, Paul K.
影响因子：
9.7
作者：
J. Seong;W. J. Kim
通讯作者：
J. Seong;W. J. Kim