Low temperature deposited Ag films exhibiting highly preferred orientations
Low temperature deposited Ag films exhibiting highly preferred orientations
复制标题
低温沉积银薄膜表现出高度择优取向
DOI：
10.1016/j.matlet.2017.11.074
复制
发表时间：
2018-02
影响因子：
3
通讯作者：
Sun Jiayi
中科院分区：
文献类型：
--
作者：
Gao Xiaoming;Hu Ming;Fu Yanlong;Weng Lijun;Liu Weimin;Sun Jiayi
Due to the crystal anisotropy, highly oriented films normally exhibit unique properties and performances. In this paper, Ag films were deposited using arc ion plating (AIP) at different substrate temperatures, substrate bias voltages and Ar pressures, and the relationship between the preferred orientation and deposition parameter of the films was investigated. The results exhibited that the preferred orientation of Ag films was influenced significantly by the deposition parameter due to the competition between the surface- and strain-energy minimization, and so both Ag films that exhibited highly preferred orientations of (1 1 1) and (2 0 0), respectively, were obtained at the optimum conditions. The relatively low friction was observed from the Ag film with highly preferred orientations of (1 1 1) because the (1 1 1) plane was the slip plane of face-centred cubic crystals.
登录
查看更多内容
影响因子：
64.8
作者：
通讯作者：
--
影响因子：
3
作者：
Harris, IL;Chambers, AR;Roberts, GT
通讯作者：
Roberts, GT
DOI：
10.1016/0022-5096(96)00022-1
发表时间：
1996-05-01
影响因子：
5.3
作者：
Thompson, CV;Carel, R
通讯作者：
Carel, R
DOI：
10.1016/c2009-0-18800-1
发表时间：
2010-04
期刊：
--
影响因子：
--
作者：
D. M. Mattox
通讯作者：
D. M. Mattox
影响因子：
64.8
作者：
Alexandra Schonning
通讯作者：
Alexandra Schonning