Nanoscale assembly of amine functionalized colloidal iron oxide.
Nanoscale assembly of amine functionalized colloidal iron oxide.
复制标题
DOI：
10.1016/j.jmmm.2009.02.080
复制
发表时间：
2009-05
影响因子：
2.7
通讯作者：
Bahadur D
中科院分区：
文献类型：
--
作者：
Barick KC;Aslam M;Prasad PV;Dravid VP;Bahadur D
我们证明了一个简单的一步高水稳定的组装胺官能化的Fe 3 O 4纳米粒子使用的Fe-氯化物前体在乙二醇介质中的乙二胺的存在下的热分解的方法。纳米组装体的平均尺寸为40± lnm，其中单个纳米颗粒为约6 nm。胺官能化的性质从FTIR、热和元素分析中是明显的。纳米组装体的饱和磁化强度和自旋回波r2分别为64.3 emu/g和314.6 mM-1 s-1。较高的弛豫率比值（r2/r1=143）表明纳米组装体是一种有前景的高效T2造影剂平台。
We demonstrate a single-step facile approach for highly water stable assembly of amine-functionalized Fe3O4 nanoparticles using thermal decomposition of Fe-chloride precursors in ethylene glycol medium in the presence of ethylenediamine. The average size of nanoassemblies is 40±1 nm, wherein the individual nanoparticles are about 6 nm. Amine functionalized properties are evident from FTIR, thermal and elemental analysis. The saturation magnetization and spin-echo r2 of the nanoassemblies were measured to be 64.3 emu/g and 314.6 mM-1s-1, respectively. The higher value of relaxivity ratio (r2/r1=143) indicates that nanoassemblies are a promising high efficiency T2 contrast agent platform.
登录
查看更多内容
影响因子：
82.9
作者：
Lee, Jae-Hyun;Huh, Yong-Min;Cheon, Jinwoo
通讯作者：
Cheon, Jinwoo
影响因子：
5
作者：
EBISU, T;WATANABE, T
通讯作者：
WATANABE, T
影响因子：
3
作者：
Nitin, N;LaConte, LEW;Bao, G
通讯作者：
Bao, G
影响因子：
64.8
作者：
Boal, AK;Ilhan, F;Rotello, VM
通讯作者：
Rotello, VM
影响因子：
6.7
作者：
Rohrer, M;Bauer, H;Weinmann, HJ
通讯作者：
Weinmann, HJ