Proposing of repair method of CFRTP by needle punching and patchbonding
针刺贴补CFRTP修复方法的提出
基本信息
- 批准号:23860045
- 负责人:
- 金额:$ 1.91万
- 依托单位:
- 依托单位国家:日本
- 项目类别:Grant-in-Aid for Research Activity Start-up
- 财政年份:2011
- 资助国家:日本
- 起止时间:2011 至 2012
- 项目状态:已结题
- 来源:
- 关键词:
项目摘要
The purpose of this study is to investigate the fracture morphology and repairbility of CFRTP. Four-point bending test was conducted to investigate the fracture morphology of CFRTP subjected to bending load. Test results showed that the local delamination was first appeared when the 2.0% of bending strain was applied. When the 2.5% of bending strain was applied, the damage of fiber due to the local buckling was observed at compression side of specimen. The effect of patch bonding on bending strength and modulus was also evaluated. Test results showed that damaged specimen would be repaired when appropriate layer of patch was bonded, and the patch bonding at compression side was more effective than that at tension side. The effect of needle punch on bending characteristics of CFRTP was also evaluated. Test results showed that the interlaminar strength of CFRTP was improved due to the delamination was supressed by needle punch. Moreover , bending strength and modulus of CFRTP repaired by needle punching and patch bonding was higher than that repaired by only patch bonding.
本研究的目的是探讨碳纤维增强塑料(CFRTP)的断裂形态和修复性能。采用四点弯曲试验研究了碳纤维增强塑料(CFRTP)在弯曲载荷作用下的断裂形貌。试验结果表明,当施加2.0%的弯曲应变时,首先出现局部分层。当施加2.5%的弯曲应变时,在压缩侧观察到由于局部屈曲引起的纤维损伤。还评估了贴片粘结对弯曲强度和模量的影响。试验结果表明,在损伤试件上粘贴适当层数的补片可以实现损伤试件的修复,且压侧补片粘贴比拉侧补片粘贴效果好。研究了针刺对CFRTP弯曲性能的影响。试验结果表明,针刺抑制了CFRTP的分层,提高了CFRTP的层间强度。针刺修补和补片粘贴修补的CFRTP的弯曲强度和弯曲模量均高于单纯补片粘贴修补的CFRTP。
项目成果
期刊论文数量(29)
专著数量(0)
科研奖励数量(0)
会议论文数量(0)
专利数量(0)
Study on Patch Bonding for Recovery of Damaged Carbon Fiber Reinforced Thermoplastics by Four-Point Bending Method
四点弯曲法修补碳纤维增强热塑性塑料修复修复的研究
- DOI:
- 发表时间:2013
- 期刊:
- 影响因子:0
- 作者:Kiyotaka Obunai;Tadao Fukuta;Koichi Ozaki;Rei Yamagishi;Masahiro Yamamoto
- 通讯作者:Masahiro Yamamoto
マイクロ波照射による廃CFRPからの炭素繊維抽出メカニズム
微波辐射从废CFRP中提取碳纤维的机理
- DOI:
- 发表时间:2012
- 期刊:
- 影响因子:0
- 作者:山岸鈴;小武内清貴;福田忠生;尾崎公一
- 通讯作者:尾崎公一
曲げ損傷を有する CF/PA6 複合材料の修繕
CF/PA6复合材料弯曲损伤的修复
- DOI:
- 发表时间:2012
- 期刊:
- 影响因子:0
- 作者:山本真大,山岸鈴;小武内清貴,福田忠生,尾崎公一
- 通讯作者:小武内清貴,福田忠生,尾崎公一
立体網目構造を有する炭素粉末の添加によるC/C複 合材料の曲げ強度および破壊じん性の向上
添加三维网络结构碳粉提高C/C复合材料的弯曲强度和断裂韧性
- DOI:
- 发表时间:2012
- 期刊:
- 影响因子:0
- 作者:三島悠一郎;荒木宏之;中原健太;Y. Mizuguchi;Akira Itabashi;小武内清貴,大窪和也,藤井透
- 通讯作者:小武内清貴,大窪和也,藤井透
曲げ損傷を受けた CFRTP の修繕性に関する基礎的研究
CFRTP弯曲损伤修复性基础研究
- DOI:
- 发表时间:2012
- 期刊:
- 影响因子:0
- 作者:山岸鈴;小武内清貴,福田忠生,尾崎公一
- 通讯作者:小武内清貴,福田忠生,尾崎公一
{{
item.title }}
{{ item.translation_title }}
- DOI:
{{ item.doi }} - 发表时间:
{{ item.publish_year }} - 期刊:
- 影响因子:{{ item.factor }}
- 作者:
{{ item.authors }} - 通讯作者:
{{ item.author }}
数据更新时间:{{ journalArticles.updateTime }}
{{ item.title }}
- 作者:
{{ item.author }}
数据更新时间:{{ monograph.updateTime }}
{{ item.title }}
- 作者:
{{ item.author }}
数据更新时间:{{ sciAawards.updateTime }}
{{ item.title }}
- 作者:
{{ item.author }}
数据更新时间:{{ conferencePapers.updateTime }}
{{ item.title }}
- 作者:
{{ item.author }}
数据更新时间:{{ patent.updateTime }}
OBUNAI Kiyotaka其他文献
OBUNAI Kiyotaka的其他文献
{{
item.title }}
{{ item.translation_title }}
- DOI:
{{ item.doi }} - 发表时间:
{{ item.publish_year }} - 期刊:
- 影响因子:{{ item.factor }}
- 作者:
{{ item.authors }} - 通讯作者:
{{ item.author }}
{{ truncateString('OBUNAI Kiyotaka', 18)}}的其他基金
Inter-laminar fracture toughness enhancement of CFRTP by using super-sonic needle punching
超声针刺增强CFRTP层间断裂韧性
- 批准号:
25870643 - 财政年份:2013
- 资助金额:
$ 1.91万 - 项目类别:
Grant-in-Aid for Young Scientists (B)
相似海外基金
熱可塑性樹脂複合材料パイプの革新的連続成形技術の開発
热塑性复合管材创新连续成型技术的开发
- 批准号:
23K26389 - 财政年份:2024
- 资助金额:
$ 1.91万 - 项目类别:
Grant-in-Aid for Scientific Research (B)
パワー半導体材料の超精密研削を実現する熱可塑性樹脂ボンド砥石の有気孔化と性能評価
功率半导体材料超精密磨削用热塑性树脂结合剂砂轮的多孔结构及性能评价
- 批准号:
24K07269 - 财政年份:2024
- 资助金额:
$ 1.91万 - 项目类别:
Grant-in-Aid for Scientific Research (C)
Development of Innovative Continuous Molding Technology for Thermoplastic Resin Composite Pipes
热塑性树脂复合管材创新连续成型技术的开发
- 批准号:
23H01696 - 财政年份:2023
- 资助金额:
$ 1.91万 - 项目类别:
Grant-in-Aid for Scientific Research (B)
真空紫外光により改質された繊維強化熱可塑性樹脂/金属異材溶着技術の開発
真空紫外光改性纤维增强热塑性树脂/金属异种材料焊接技术开发
- 批准号:
23K13582 - 财政年份:2023
- 资助金额:
$ 1.91万 - 项目类别:
Grant-in-Aid for Early-Career Scientists
PEEKと弾性を有する熱可塑性樹脂を用いたフルデジタルノンメタル部分床義歯の開発
使用 PEEK 和弹性热塑性树脂开发全数字化非金属局部义齿
- 批准号:
22K17132 - 财政年份:2022
- 资助金额:
$ 1.91万 - 项目类别:
Grant-in-Aid for Early-Career Scientists
粘弾性・粘塑性解析に基づく炭素繊維強化熱可塑性樹脂の強度解析
基于粘弹性/粘塑性分析的碳纤维增强热塑性树脂强度分析
- 批准号:
21K03753 - 财政年份:2021
- 资助金额:
$ 1.91万 - 项目类别:
Grant-in-Aid for Scientific Research (C)
融点が46℃の熱可塑性樹脂の常温における強度評価
熔点46℃热塑性树脂室温强度评价
- 批准号:
20H01105 - 财政年份:2020
- 资助金额:
$ 1.91万 - 项目类别:
Grant-in-Aid for Encouragement of Scientists
固定素材に熱可塑性樹脂を応用した鏡視下手根管開放術の術後指導効果の検証
以热塑性树脂为固定材料进行关节镜腕管松解术术后引导的有效性验证
- 批准号:
19K19627 - 财政年份:2019
- 资助金额:
$ 1.91万 - 项目类别:
Grant-in-Aid for Early-Career Scientists
Development of automobile shock absorbing member by made of high strength glass fiber and in-situ polymerizable thermoplastic resin
高强度玻璃纤维与原位聚合热塑性树脂汽车减震件的研制
- 批准号:
18K04637 - 财政年份:2018
- 资助金额:
$ 1.91万 - 项目类别:
Grant-in-Aid for Scientific Research (C)
In-situ界面特性を考慮した連続繊維強化熱可塑性樹脂複合材料の成形設計
考虑原位界面性能的连续纤维增强热塑性树脂复合材料成型设计
- 批准号:
17KK0113 - 财政年份:2017
- 资助金额:
$ 1.91万 - 项目类别:
Fund for the Promotion of Joint International Research (Fostering Joint International Research)