RESEARCH ON CERAMICS BATTERIES

陶瓷电池的研究

• 批准号: 10555311
• 负责人: KANNO Ryoji
• 金额: $ 8.51万
• 依托单位: KOBE UNIVERSITY
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (B)
• 财政年份: 1998
• 资助国家: 日本
• 起止时间: 1998 至 2000
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/en/grant/KAKENHI-PROJECT-10555311/
• 关键词: THIO-LISICON; LITHIUM ION CONDUCTOR; LITHIUM SECONDARY BATTERY; ALL SOLID STATE CELL; 超イオン導電体; リチウム固体電解質

The new crystalline material-family, the 'thio-LISICON' (Lithium SuperIonic CONductor), was found in the Li_2S-GeS_2-P_2S_s system. The solid solution at x = 0.75 in Li_<4-x>Ge_<1-2>P_2S_4 shows the highest conductivity of 2.2 x 10^<-3> Scm^<-1> at 25℃ amongst sintered ceramics, together with negligible electronic conductivity, high electrochemical stability, no reaction with lithium metal, and no phase transition up to 500℃. Its material-design concepts of changing constituent ions with various ionic radii, valence, and polarizability are studied.

在Li_2S-GeS_2-P_2S_s体系中发现了新的晶体材料家族“硫代lisicon”（锂超离子导体）。在烧结陶瓷中，x = 0.75时的固溶体Li_<4-x>Ge_<1-2>P_2S_4在25℃时的电导率最高，为2.2 × 10^<-3> Scm^<-1>，电导率可忽略不计，电化学稳定性高，不与金属锂发生反应，在500℃前不发生相变。研究了改变不同离子半径、价态和极化率的组成离子的材料设计概念。

项目成果

R.Kanno 他: "Synthesis and Structure of Lithium Manganese Oxide spinel, LiMn_2O_<4-δ> (0【less than or equal】δ【less than or equal】0.27)"J.Power Sources. (印刷中).

R. Kanno等人：“锂锰氧化物尖晶石的合成和结构，LiMn_2O_<4-δ>（0【小于或等于】δ【小于或等于】0.27）”J. Power Sources（出版中）。 。

R.Kanno 他: "The relationships between phase, structure and electrochemical properties for lithium manganese spinels"J.Power Sources. 81-82. 542-546 (1999)

R. Kanno 等人：“锂锰尖晶石的相、结构和电化学性质之间的关系”J. Power Sources 81-82 (1999)。

R.Kanno 他: "Synthesis of New Lithium Ionic Conductor, Thio-LISIOCON--Lithium Germanium Sulfide System"Solid State Ionics. 130(1-2). 97-103 (2000)

R. Kanno 等人：“新型锂离子导体的合成，Thio-LISIOCON - 锂锗硫化物系统”固态离子学 130(1-2) (2000)。

R. Kanno, 他: "Thio-LISICON-lithium Germanium Sulfied System"Solid State Ionics. (印刷中). (2000)

R. Kanno 等人：“硫代-LISICON-锂锗硫化系统”固态离子学（印刷中）。

R.Kanno 他: "Synthesis and Structure of Lithium Manganese Oxide spinel, LiMn_2O_<4-δ>(0【less than or equal】δ【less than or equal】0.27)"J.Power Sources. (印刷中).

R. Kanno 等：“锂锰氧化物尖晶石的合成和结构，LiMn_2O_<4-δ>（0【小于或等于】δ【小于或等于】0.27）”J. Power Sources（出版中）。 。