Development of environmentally adaptable processes for synthesizing functional particles

开发环境适应性强的功能颗粒合成工艺

• 批准号: 23246134
• 负责人: KONNO Mikio
• 金额: $ 25.79万
• 依托单位: Tohoku University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (A)
• 财政年份: 2011
• 资助国家: 日本
• 起止时间: 2011-04-01 至 2014-03-31
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/en/grant/KAKENHI-PROJECT-23246134/
• 关键词: ナノ材料; ポリマー; 微粒子; 単分散; 静電相互作用

Environmentally adaptable synthetic processes were studied for polymer particles with low polydispersity. The synthetic processes that use water as a solvent could prepare monodisperse particles in a wide size range from 50 nm to several micron meters. Since neither polymer dispersant nor a large amount of surfactants was added to the synthetic system, surfaces of polymer particles obtained in the process were highly pure. The pure surfaces of polymer particles can be advantages when the polymer particles are used as components for functional composite particles.

研究了低多分散性聚合物颗粒的环境适应性合成工艺。使用水作为溶剂的合成工艺可以制备单分散颗粒，其尺寸范围从50纳米到几微米不等。由于在合成体系中既没有添加聚合物分散剂，也没有添加大量的表面活性剂，因此在该过程中获得的聚合物颗粒表面纯度很高。当聚合物颗粒用作功能复合颗粒的组分时，聚合物颗粒的纯净表面具有优势。

项目成果

Asymmetric Composite Dumbbells to be Oriented and Assembled by External Fields

由外部场定向和组装的不对称复合哑铃

• 作者: D. NAGAO;K. HAYASAKA;M. SUGIMOTO;M. KONNO
• 通讯作者: M. KONNO

水相析出重合への高分子電解質とイオン性界面活性剤の共添加による単分散性ポリマー粒子の合成

水相沉淀聚合共添加聚电解质和离子表面活性剂合成单分散聚合物颗粒

• 发表时间: 2011
• 作者: 川野部潤;石井治之;長尾大輔;今野幹男
• 通讯作者: 今野幹男

粒子組成と形態を操る液相微粒子合成

控制颗粒组成和形态的液相微粒合成

• 发表时间: 2011
• 作者: D. Nagao;K. Hayasaka;M. Sugimoto;M. Konno;長尾大輔,西眞理子,岡田絢子,石井治之,今野幹男;長尾大輔
• 通讯作者: 長尾大輔

Preparation of oil-containing, polymeric particles having a single depression with various shapes

• DOI: 10.1039/c2sm07109f
• 发表时间: 2012-04
• 期刊: Soft Matter
• 影响因子: 3.4
• 作者: T. Ohta;D. Nagao;H. Ishii;M. Konno

東北大学大学院工学研究科化学工学専攻 今野研究室ＨＰ

东北大学研究生院工学部化学工程系绀野实验室HP