Evaluation of Exterior Coatings (Minium Color) for Development of the Conservation of Historic Wooden Building

历史木建筑保护发展的外墙涂料（最小颜色）评价

• 批准号: 05555163
• 负责人: NISHIURA Tadateru
• 金额: $ 6.53万
• 依托单位: Tokyo National Research Institute of Cultural Properties
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Developmental Scientific Research (B)
• 财政年份: 1993
• 资助国家: 日本
• 起止时间: 1993 至 1995
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-05555163/
• 关键词: Conservation of Cultural Property; Historic Wooden Building; Exterior Painting; Minium Color Painting; Synthetic Resins; Durability

Exposure test and accelerated deterioration test with weather-o-meter were performed on three kinds of paintings (total of seventeen) : traditional material (a mixture of minium <red lead> and animal glue) : recently developed high durable architectural paints for exterior use (a mixture of synthetic resin with organic pigment) : and a mixture of clear synthetic resin and minium. Exposure places are the roof of the Tokyo National Research Institute of Cultural Properties and the site of Hinomisaki Shrine (Taishamachi, Shimane prefecture).The results were studied, analyzed comparatively and discussed at the end. The summary of the test is as follows :・Tranditional material (minium mixed with animal glue) exfoliated easily and was found to be low in durability.・Synthetic resin paint in general was found to be much higher in durability. Especially, organo-silicone type and fluorine-containing type resins exhibited highest durability amoungst the test pieces.・Paint contains minium tends to change color more easily : the blacking seen on the paint mixture of synthtic resin with minium is peculiar. such blacking does not happen in the standarized synthetic resin paints.・Test result showed that primer treatment, though difference in degree, is quite effective.

对三种涂料（共十七种）进行了暴露试验和老化加速试验：传统材料（橡胶和动物胶的混合物<red lead>）、新近开发的高耐久性建筑外墙涂料（合成树脂和有机颜料的混合物）和透明合成树脂和橡胶的混合物。曝光地点为东京国立文化财产研究所屋顶和日之崎神社遗址（岛根县大山町），最后对结果进行了研究、比较分析和讨论。测试总结如下：·透明材料（与动物胶混合的胶水）容易剥落，并且发现耐久性低。·合成树脂涂料一般被发现在耐久性上高得多。特别是有机硅型和含氟型树脂在测试件中表现出最高的耐久性。·油漆中含有重金属，更容易变色：在重金属树脂和重金属的油漆混合物上看到的黑色是很奇怪的。在标准化的合成树脂涂料中不会发生这种变黑。试验结果表明，引物处理效果较好，但程度不同。

项目成果

西浦忠輝 他2名: "古建築の保存を目的とした外装塗装の物性評価" 第12回日本文化財科学会大会研究発表要旨集. 34-35 (1995)

Tadateru Nishiura 等 2 人：“以保护古建筑为目的的外墙涂料物理性能评估”日本文化财产学会第 12 届年会研究报告摘要 34-35（1995 年）。

西浦忠輝他2名: "丹色塗装の屋外曝露試験" 第17回古文化財科学研究会大会講演要旨集. 94-95 (1995)

西浦忠辉等2人：《红色涂料的户外暴露试验》第17届古代文化遗产科学研究会议摘要94-95（1995）。

西浦忠輝他2名: "古建築の外装塗装の物性に関する研究(III)-丹色塗装の屋外曝露試験(2)-" 保存科学. 第35号. 21-31 (1996)

西浦忠辉等2人：“旧建筑外墙涂料物理性能研究（三）-红色涂料的户外暴露试验（2）-”保护科学第35期21-31（1996）。

西浦忠輝他2名: "丹色塗装の屋外曝露試験〔II〕" 第18回文化財保存修復学会大会講演要旨集. 34-35 (1996)

Tadateru Nishiura 等 2 人：“红色涂料的户外暴露测试 [II]”第 18 届文化财产保护与修复学会会议摘要 34-35（1996 年）。