Development of alloy plating with high corrosion resistivity without chromate treatments-Addition of self healing property by valence fluctuation

无需铬酸盐处理的高耐腐蚀性合金镀层的开发-通过价数波动增加自修复性能

• 批准号: 19360340
• 负责人: HIRATO Tetsuji
• 金额: $ 12.98万
• 依托单位: Kyoto University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (B)
• 财政年份: 2007
• 资助国家: 日本
• 起止时间: 2007 至 2009
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-19360340/
• 关键词: 表面処理; 合金電析; 非水溶媒; アルミニウム合金; 電気めっき; イオン液体

A new environmentally-friendly surface finishing process has been developed by combining electrodeposition and heat treatment. By using AlCl_3-ZnCl_2-dimethylsulfone (DMSO_2) molten electrolytes, Al-Zn alloys were obtained. By addition of MnCl_2 to the electrolytes, Al-Zn-Mn alloy deposits with smooth surface were obtained. Codeposition of Mn led to finer grain size and inhibited Zn metal deposition.

将电沉积与热处理相结合，开发了一种新的环保型表面处理工艺。采用AlCl_3-ZnCl_2-二甲基砜（DMSO_2）熔融电解液制备了Al-Zn合金。在电解液中加入MnCl_2，可获得表面光滑的Al-Zn-Mn合金镀层。Mn的共沉积导致晶粒细化，抑制了Zn金属的沉积。

项目成果

Electrodeposition of Zn-Al Alloys from AlCl3-ZnCl2-Dimethilsulfone Molten Electrolytes

AlCl3-ZnCl2-二甲基砜熔融电解质电沉积锌铝合金

• 发表时间: 2009
• 期刊: ECS Transactions 25
• 作者: Kazumi Takenaka;Yuji Mizuta;Tetsuji Hirato
• 通讯作者: Tetsuji Hirato

ジメチルスルホン-AlCl3-ZnCl2浴を用いるAl-Zn合金電析

二甲砜-AlCl3-ZnCl2镀液电沉积Al-Zn合金

• 发表时间: 2008
• 作者: 水田雄二;他
• 通讯作者: 他

有機溶媒からのアルミニウム電析と熱処理を利用する耐熱表面処理

使用有机溶剂电沉积铝和热处理进行耐热表面处理

• 发表时间: 2010
• 作者: 塩見卓;他
• 通讯作者: 他

非水溶媒を用いるアルミニウム電気めっき

使用非水溶剂电镀铝

• 发表时间: 2009
• 作者: 竹中和己;et al.;平藤哲司
• 通讯作者: 平藤哲司

電析法によるAl-Zn合金薄膜の作製

电沉积法制备Al-Zn合金薄膜

• 发表时间: 2010
• 作者: 竹中和己;他
• 通讯作者: 他