A study on defect formation in hydrogen absorbing alloys during hydrogen absorption-desorption cycling
吸氢合金吸放氢循环过程中缺陷形成的研究
基本信息
- 批准号：20560615
- 负责人：
- 金额：$ 2.91万
- 依托单位：
- 依托单位国家：日本
- 项目类别：Grant-in-Aid for Scientific Research (C)
- 财政年份：2008
- 资助国家：日本
- 起止时间：2008 至 2010
- 项目状态：已结题
- 来源：
- 关键词：
项目摘要
Hydrogen absorbing alloys are ingredients essential for switching to clean energy. LaNi_5-based alloys are most frequently used as hydrogen storage materials for electrodes of rechargeable batteries, purification of hydrogen and so on, and it is known that their reversible hydrogen absorbing capacities are decreased by the hydrogen absorption-desorption cycling. In this work we have studied, with positron lifetime spectroscopy, the degradation of LaNi_5-based alloys during the pressure-induced cycling at 248K, and revealed that the decrease in hydrogen absorbing capacity is attributed at least partly to lattice defects formed during hydriding.
吸氢合金是转换为清洁能源的关键成分。LaNi5基合金是二次电池电极、氢气净化等领域最常用的储氢材料，其可逆吸放氢容量因吸放氢循环而降低。在本工作中，我们用正电子寿命谱研究了LaNi5基合金在248K的压力诱导循环过程中的退化，发现吸氢能力的下降至少部分归因于氢化过程中形成的晶格缺陷。
项目成果
期刊论文数量（0）
专著数量（0）
科研奖励数量（0）
会议论文数量（0）
专利数量（0）
Behavior of vacancy formation and recovery during hydrogenation cycles in LaNi_<4. 93> Sn_<0. 27>
LaNi_<4氢化循环过程中空位形成和恢复的行为。
- DOI：
- 发表时间：2009
- 期刊：
- 影响因子：6.2
- 作者：Kouji Sakaki;Ryosuke Date;Masataka Mizuno;Hideki Araki;Yumiko Nakamura;Yasuharu Shirai;Robert C. Bowman Jr.;Etsuo Akiba
- 通讯作者：Etsuo Akiba
Behavior of vacancy formation and recovery during hydrogenation cycles in LaNi4.93Sn0.27
LaNi4.93Sn0.27 加氢循环过程中空位形成和恢复的行为
- DOI：
- 发表时间：2009
- 期刊：
- 影响因子：6.2
- 作者：安里光裕;星野敏春;川上和人;Kouji Sakaki
- 通讯作者：Kouji Sakaki
First-principles study of vacancy formation in LaNi_5
LaNi_5空位形成的第一性原理研究
- DOI：
- 发表时间：2008
- 期刊：
- 影响因子：0
- 作者：Masataka Mizuno;Hideki Araki;Yasuharu Shirai
- 通讯作者：Yasuharu Shirai
The effect of substitutional elements (Al, Co) in LaNi4.5M0.5 on the lattice defect formation in the initial hydrogenation and dehydrogenation
- DOI：10.1016/j.jallcom.2008.05.044
- 发表时间：2009-04
- 期刊：
- 影响因子：6.2
- 作者：K. Sakaki;E. Akiba;M. Mizuno;H. Araki;Y. Shirai
- 通讯作者：K. Sakaki;E. Akiba;M. Mizuno;H. Araki;Y. Shirai
Electronic Structure and Bonding in Amorphous Zr_67Ni_33 and Zr_67Cu_33
非晶Zr_67Ni_33和Zr_67Cu_33的电子结构和成键
- DOI：
- 发表时间：2008
- 期刊：
- 影响因子：0
- 作者：大橋栄久;他;Kazuki Sugita
- 通讯作者：Kazuki Sugita
{{
item.title }}
{{ item.translation_title }}
- DOI：
{{ item.doi }} - 发表时间：
{{ item.publish_year }} - 期刊：
- 影响因子：{{ item.factor }}
- 作者：
{{ item.authors }} - 通讯作者：
{{ item.author }}
数据更新时间：{{ journalArticles.updateTime }}
{{ item.title }}
- 作者：
{{ item.author }}
数据更新时间：{{ monograph.updateTime }}
{{ item.title }}
- 作者：
{{ item.author }}
数据更新时间：{{ sciAawards.updateTime }}
{{ item.title }}
- 作者：
{{ item.author }}
数据更新时间：{{ conferencePapers.updateTime }}
{{ item.title }}
- 作者：
{{ item.author }}
数据更新时间：{{ patent.updateTime }}
ARAKI Hideki其他文献
ARAKI Hideki的其他文献
{{
item.title }}
{{ item.translation_title }}
- DOI：
{{ item.doi }} - 发表时间：
{{ item.publish_year }} - 期刊：
- 影响因子：{{ item.factor }}
- 作者：
{{ item.authors }} - 通讯作者：
{{ item.author }}
{{ truncateString('ARAKI Hideki', 18)}}的其他基金
Positron lifetime study on vacancy behavior in bcc-base intermetallics
BCC基金属间化合物空位行为的正电子寿命研究
- 批准号：
18560644 - 财政年份：2006
- 资助金额：
$ 2.91万 - 项目类别：
Grant-in-Aid for Scientific Research (C)
Theoretical analysis and empirical tests on effects of defoliation that alleviate loss of production in doughted crops.
关于落叶对减轻受困作物产量损失影响的理论分析和实证检验。
- 批准号：
18688019 - 财政年份：2005
- 资助金额：
$ 2.91万 - 项目类别：
Grant-in-Aid for Young Scientists (A)
Study of pre-martensitic phenomena in shape memory alloys by positron annihilation lifetime spectroscopy
正电子湮没寿命谱研究形状记忆合金中的预马氏体现象
- 批准号：
13650720 - 财政年份：2001
- 资助金额：
$ 2.91万 - 项目类别：
Grant-in-Aid for Scientific Research (C)
相似海外基金
照射誘起欠陥挙動のポンププローブ型陽電子消滅分光による評価
使用泵浦探针正电子湮没光谱评估辐照引起的缺陷行为
- 批准号：
23K23273 - 财政年份：2024
- 资助金额：
$ 2.91万 - 项目类别：
Grant-in-Aid for Scientific Research (B)
その場陽電子消滅法による鉄鋼における水素脆化関連原子空孔の特定
原位正电子湮灭法识别钢中与氢脆相关的空位
- 批准号：
24K08015 - 财政年份：2024
- 资助金额：
$ 2.91万 - 项目类别：
Grant-in-Aid for Scientific Research (C)
Hydrogen-induced vacancies in tungsten studied by in-situ analysis of vacancies using positron annihilation measurements under hydrogen charging
利用充氢下的正电子湮没测量对空位进行原位分析，研究钨中氢引起的空位
- 批准号：
23K03359 - 财政年份：2023
- 资助金额：
$ 2.91万 - 项目类别：
Grant-in-Aid for Scientific Research (C)
Evaluation of irradiation-induced defect behaviors by pump-probe positron annihilation spectroscopy
通过泵浦探针正电子湮没光谱评估辐照引起的缺陷行为
- 批准号：
22H02005 - 财政年份：2022
- 资助金额：
$ 2.91万 - 项目类别：
Grant-in-Aid for Scientific Research (B)
Development of a positron annihilation apparatus with sub-mm space resolution for the detection of nm-size open volume
开发具有亚毫米空间分辨率的正电子湮没装置，用于检测纳米尺寸开放体积
- 批准号：
21K18812 - 财政年份：2021
- 资助金额：
$ 2.91万 - 项目类别：
Grant-in-Aid for Challenging Research (Exploratory)
Gas element-vacancy complexes investigated by electron momentum distribution analysis using a combination of positron annihilation and first-principles calculations
结合正电子湮灭和第一性原理计算，通过电子动量分布分析研究气体元素-空位复合物
- 批准号：
20K03902 - 财政年份：2020
- 资助金额：
$ 2.91万 - 项目类别：
Grant-in-Aid for Scientific Research (C)
Study of metal fatigue using ultra-precise ∆T0 measurement system for positron annihilation lifetime spectra
利用超精密技术研究金属疲劳
- 批准号：
20K12506 - 财政年份：2020
- 资助金额：
$ 2.91万 - 项目类别：
Grant-in-Aid for Scientific Research (C)
EAGER: Collaborative Research: Positron annihilation spectroscopy of Earth materials:A combined materials characterization approach
EAGER：合作研究：地球材料的正电子湮灭光谱：一种组合材料表征方法
- 批准号：
2001444 - 财政年份：2019
- 资助金额：
$ 2.91万 - 项目类别：
Standard Grant
RII Track-4: Use of Positron Annihilation Lifetime Spectroscopy to Engineer Membrane Selective Layers
RII Track-4：使用正电子湮没寿命光谱来设计膜选择性层
- 批准号：
1928812 - 财政年份：2019
- 资助金额：
$ 2.91万 - 项目类别：
Standard Grant
Development of portable positron annihilation lifetime spectrometer and its in situ applications
便携式正电子湮灭寿命谱仪研制及其原位应用
- 批准号：
19H02742 - 财政年份：2019
- 资助金额：
$ 2.91万 - 项目类别：
Grant-in-Aid for Scientific Research (B)