The research of development of reminral ization activator with long term remaining performance on root dentin surface

牙根牙本质表面长效再矿化激活剂的研制

• 批准号: 20791379
• 负责人: OKUYAMA Katsushi
• 金额: $ 2.66万
• 依托单位: Hokkaido University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2008
• 资助国家: 日本
• 起止时间: 2008 至 2010
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-20791379/
• 关键词: 根面象牙質; 再石灰化; 根面保持; pHサイクル; フッ素溶出

The purpose of this research was to evaluate the fluoride-releasing coating material, which have the performance of long-term remaining on root dentin surface due to caries prevention. The results of this study showed that amount of fluoride release from the coating material was larger than that of current material. Remineralization of root dentin (the measure of caries prevention) by the coating material was indicated more than that of other materials. Fluoride application was made improve bonding strength between dentin and dental material. Then fluoride ion was detected on interface between dentin and dental material.

本研究的目的是评价一种具有防龋性的长期滞留在根面牙本质表面的氟化物释放涂层材料。研究结果表明，涂层材料的氟化物释放量大于现有材料。涂层材料对根面牙本质(防龋剂)的再矿化作用优于其他材料。加氟可提高牙本质与牙科材料的粘结强度。然后在牙本质与牙科材料的界面上检测到氟离子。

项目成果

充填1年後におけるフッ素含有材料の齲蝕抑制効果

含氟材料充填一年后的防龋效果

• 发表时间: 2010
• 作者: 小松久憲;松田康裕;大木彩子;橋本直樹;奥山克史;山本洋子;能町正治;菅谷頼仁;安田啓介;佐藤隆博;江夏昌志;船戸良基;小松久憲;船戸良基;小島健太郎
• 通讯作者: 小島健太郎

フッ素含有材料からの歯質への長期フッ素取り込み量

牙齿结构从含氟材料中长期吸收氟化物

• 发表时间: 2010
• 作者: 小松久憲、船戸良基、奥山克史;他
• 通讯作者: 他

核反応による齲蝕歯中のフッ素濃度分布の測定

核反应测量龋齿中氟浓度分布

• 发表时间: 2009
• 作者: 小松久憲;山本洋子;奥山克史;他
• 通讯作者: 他

Fluoride analysis of human enamel around fluoride-containing materials under different pH-cycling by μ-PIGE/PIXER system

μ-PIGE/PIXER系统在不同pH循环下对含氟材料周围的人牙釉质进行氟化物分析

• 发表时间: 2010
• 作者: H Komatsu;K Okuyama;他
• 通讯作者: 他

フッ素含有材料の乳酸溶液へのフッ素溶出

含氟物质溶入乳酸溶液中的氟

• 发表时间: 2009
• 作者: 小島健太郎、小松久憲、奥山克史;他
• 通讯作者: 他