On The Strength Characteristic and Carbonation of Concrete in Aged Structure

老化结构混凝土的强度特性及碳化研究

• 批准号: 20860087
• 负责人: TAMAI Takayuki
• 金额: $ 2.1万
• 依托单位: Yonago National College of Technology
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (Start-up)
• 财政年份: 2008
• 资助国家: 日本
• 起止时间: 2008 至 2009
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-20860087/
• 关键词: 中性化; 高寿命化; 実大試験体; 長期暴露試験; 圧縮強度; 非破壊検査; 長寿命化; 暴露試験

The result of built two wall models of 3.0m in height, 7.4m in width. The materials of the concrete were Porto land cement, the water ratio was 40% and 50%. In this year, I went fresh properties, compressive strength and Non Destructive Inspection (rebound number, Supersonic wave communication speed) of the concrete. I stored materials (cement, fine aggregate, coarse aggregate) which I used to be able to perform a reproduction experiment 10 years later or 20 years later.

结果建立了两个高3.0m、宽7.4m的墙体模型。混凝土的材料为波尔图陆地水泥，水化率为40%和50%。在这一年里，我去了混凝土的新鲜性能，抗压强度和无损检测（回弹数，超声波通信速度）。我储存的材料（水泥，细骨料，粗骨料），我曾经能够进行复制实验10年后或20年后。