Mechanism of Dissolution and Deposition for Electrolytes underNano-Restricted Conditions

纳米限制条件下电解质的溶解和沉积机理

• 批准号: 20750013
• 负责人: OHKUBO Takahiro
• 金额: $ 2.58万
• 依托单位: Okayama University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2008
• 资助国家: 日本
• 起止时间: 2008 至 2009
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-20750013/
• 关键词: 表面・界面物性; 炭素材料; X線吸収分光; 電解質水溶液; 液相吸着; ナノスペース; ナノ材料; X線; イオン; 溶液; 吸着; ミクロ孔; 活性炭素繊維; ナノ溶液; XAFS; XANES; 亜鉛イオン; 溶媒和構造; ナノ空間

The hydration structure of zinc ions confined in nanospaces of activated carbons was determined by XAFS and powder XRD measurements. XAFS spectra indicate that the distorted hydration structure whose structure is remarkably different from that in the bulk aqueous solution is formed in the nanospace. In addition, XRD band at d=2.0 nm was appeared for the aqueous solution confined in the nanospace whose average pore width is 0.7 nm, stemming from the ordering of molecular assembly of aqueous solution of zinc acetate.

用XAFS和XRD研究了锌离子在活性炭纳米空间中的水化结构。XAFS谱表明，在纳米空间中形成了与本体水溶液结构明显不同的畸变水化结构。此外，在平均孔径为0.7nm的纳米空间中，乙酸锌水溶液在d= 2.0nm处出现XRD谱带，这是由于乙酸锌水溶液分子组装有序化的结果。

项目成果

細孔内の構造からみたナノ溶液化学(招待講演)

从孔内结构看纳米溶液化学（特邀报告）

• 发表时间: 2008
• 作者: Nagasawa;Yutaka; Itoh;Tsuyoshi; Yasuda;Masakazu; Ishibash;Yukihide; Ito;Syoji; Miyasaka;Hiroshi;大久保貴広;大久保貴広
• 通讯作者: 大久保貴広

固体細孔内の電解質溶液-ナノ溶液-

固体孔隙中的电解质溶液-纳米溶液-

• 发表时间: 2009
• 期刊: Adsorption News 23
• 作者: 山田剛司;磯部美緒;高野康弘;渋田昌弘;宗像利明;M.Wakisaka;大久保貴広
• 通讯作者: 大久保貴広

活性炭ミクロ孔内における亜鉛イオンの水和構造

活性炭微孔中锌离子的水合结构

• 发表时间: 2010
• 作者: 大久保貴広;黒田泰重
• 通讯作者: 黒田泰重

表面で囲まれた微細な空間-ナノ空間の化学-

由表面包围的微小空间 - 纳米空间的化学 -

• 发表时间: 2009
• 作者: Nagasawa;Yutaka; Itoh;Tsuyoshi; Yasuda;Masakazu; Ishibash;Yukihide; Ito;Syoji; Miyasaka;Hiroshi;大久保貴広
• 通讯作者: 大久保貴広

ナノスペースにおける溶液構造

纳米空间中的溶液结构

• 发表时间: 2008
• 作者: Syoji Ito;Kou Itoh;Takatsugu Kusumi;Kentaro Maeda;Satoshi Takei;Hiroshi Miyasaka;大久保貴広
• 通讯作者: 大久保貴広