Development of three-dimensional orientation analysis method by using high-flux synchrotron X-ray

高通量同步加速器X射线三维取向分析方法的开发

• 批准号: 20760466
• 负责人: KOBAYASHI Masakazu
• 金额: $ 1.83万
• 依托单位: Toyohashi University of Technology
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2008
• 资助国家: 日本
• 起止时间: 2008 至 2009
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-20760466/
• 关键词: 放射光; トモグラフィー; X線回折; 結晶方位; アルミニウム合金; 三次元

For the purpose of deformation and fracture analysis in polycrystalline materials like a metal, the method that measure crystallographic orientation within a sample non-destructively has been developed. The orientation maps of an aluminum alloy were investigated using European and Japanese synchrotron radiation facilities. Inhomogeneous deformation depending on crystallographic orientation was confirmed comparing grain orientation map with strain distribution after deformation in three-dimension.

为了对金属等多晶材料进行变形和断裂分析，发展了一种非破坏性地测量样品中晶体取向的方法。利用欧洲和日本的同步辐射装置研究了铝合金的取向图。通过对晶粒取向图和变形后应变分布的三维比较，证实了非均匀变形取决于晶体取向。

项目成果

放射光を利用したアルミニウム合金の変形3D解析

利用同步辐射对铝合金变形进行 3D 分析

• 发表时间: 2009
• 作者: 小林正和;H.F.Poulsen;戸田裕之;大川嘉一
• 通讯作者: 大川嘉一

3D-XRDによる3D結晶方位解析

使用 3D-XRD 进行 3D 晶体取向分析

• 发表时间: 2009
• 作者: 小林正和;戸田裕之
• 通讯作者: 戸田裕之