Creation of Wire Electrical Discharge Machined Surface without Cracks in Cemented Carbide

硬质合金无裂纹线放电加工表面的形成

• 批准号: 21560112
• 负责人: TAMURA Takeo
• 金额: $ 1.75万
• 依托单位: Niigata University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2009
• 资助国家: 日本
• 起止时间: 2009 至 2011
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-21560112/
• 关键词: 超硬合金; ワイヤ放電加工; 溶融再凝固層; クラックレス; SI-cut; 表面改質; 浸漬方式; 無電解電源

As a method of processing cemented carbide, wire electrical discharge machining(WEDM) is generally used. However, typical surface defects, such as cracks, microcraters and recast layer, lead to a decreased surface integrity. Thus, an on-the-machine surface modification technology in WEDM, for the complete elimination of surface defects, was developed in this study. As a result, the surface defects generated by WEDM could be completely eliminated by incorporating SI-cut into WEDM. Thus, this surface modification technology is effective for finishing cemented carbide machined by WEDM.

作为加工硬质合金的方法，通常使用电火花线切割加工（WEDM）。然而，典型的表面缺陷，如裂纹，微坑和重铸层，导致降低的表面完整性。因此，在本研究中，开发了一种线切割加工中的在机表面改性技术，以完全消除表面缺陷。结果表明，电火花线切割加工中引入SI切割，可以完全消除线切割加工中产生的表面缺陷。因此，该表面改性技术是电火花线切割加工硬质合金的有效方法。

项目成果

ワイヤ放電加工によるオンザマシン表面改質技術の開発

利用电火花线切割加工在机表面改性技术的开发

• 发表时间: 2012
• 期刊: 電気加工学会誌
• 作者: 田村武夫;金子倉之介
• 通讯作者: 金子倉之介

ワイヤ放電加工された超硬合金ダイの研磨に関する研究

电火花线切割加工硬质合金模具抛光研究

• 发表时间: 2011
• 作者: 森山佑蔵;田村武夫
• 通讯作者: 田村武夫

ワイヤ放電加工におけるオンザマシン表面改質技術の表面健全性

电火花线切割机上表面改性技术的表面完整性

• 发表时间: 2010
• 作者: 杉田博紀;田村武夫
• 通讯作者: 田村武夫