Basic Research to Develop Dual Multi-phase Intermetallic Alloys as Next-generation Type Heat Resistant Materials

开发双多相金属间合金作为下一代耐热材料的基础研究

• 批准号: 21226016
• 负责人: TAKASUGI Takayuki
• 金额: $ 66.14万
• 依托单位: Osaka Prefecture University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (S)
• 财政年份: 2009
• 资助国家: 日本
• 起止时间: 2009 至 2012
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-21226016/
• 关键词: 金属間化合物; 耐熱材料; 合金設計; 複相組織; 超合金; 組織安定性; 熱安定性; Ni3Al; Ni3V; Ni_3Al; Ni_3V

For two-phase intermetallic alloys composed of two kinds of Ni3X-type compounds, alloy design, microstructural development and stabilities of microstructures and constituent phases were studied, seeking the alloying elements and their optimum contents enhancing high-temperature properties such as mechanical and environment-proof properties. Also, the primary fabrication processes by melting/casting and powder metallurgy as well as the secondary fabrication processes by heat treatment, machining and surface modification were developed. In collaboration with industries, the present two-phase intermetallic alloys were applied to various kinds of high-temperature structural, wear resistance and corrosion resistance materials.

针对由两种Ni3X型化合物组成的两相金属间化合物合金，研究了合金设计、显微组织发展、显微组织和成分相的稳定性，寻找提高高温力学性能和环境保护性能的合金元素及其最佳含量。开发了熔铸和粉末冶金的一次制造工艺，以及热处理、机械加工和表面改性的二次制造工艺。与工业界合作，目前的两相金属间化合物合金被应用于各种高温结构、耐磨和耐腐蚀材料。

项目成果

Ｎｉ基合金、それを用いた摩擦撹拌接合用ツール及びその製造方法

镍基合金、使用其的搅拌摩擦焊工具及其制造方法

• 发表时间: 2012

Taを添加したNi_3(Si,Ti)金属間化合物合金の合金化挙動

添加Ta的Ni_3(Si,Ti)金属间合金的合金化行为

• 发表时间: 2011
• 作者: Honjoh;S. and Nishida;E;今城大貴
• 通讯作者: 今城大貴

Ni基超・超合金の組織と機械的性質に及ばすTiC添加の効果

TiC添加对镍基高温合金组织和力学性能的影响

• 发表时间: 2010
• 作者: 近藤孝文;岩松和宏;田口光正;倉島俊;楊金峰;菅晃一;柴田裕実;吉田陽一;北浦祐太
• 通讯作者: 北浦祐太

Li_2型金属間化合物圧廷板の集合組織と粒界性格分布(招待講演)

Li_2型金属间化合物板材的织构和晶界特征分布（特邀报告）

• 发表时间: 2009
• 作者: S.Taguchi;鍵本純子;T.Ichikawa;T.Kato;大野弘幸;金野泰幸
• 通讯作者: 金野泰幸

Ni_3X型GCP相における合金元素の置換挙動

Ni_3X型GCP相中合金元素的替代行为

• 发表时间: 2009
• 作者: Hotta;A.;白尾瑞基;杉村蛍子
• 通讯作者: 杉村蛍子