Surface modification of titanium by pack cementation process for improvement of bone compatibility

通过包埋工艺对钛进行表面改性以改善骨相容性

• 批准号: 21760574
• 负责人: UEDA Kyosuke
• 金额: $ 2.66万
• 依托单位: Tohoku University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2009
• 资助国家: 日本
• 起止时间: 2009 至 2010
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-21760574/
• 关键词: チタン; 表面処理; リン酸カルシウム; パックセメンテーション法; 密着力; アパタイト; 生体外評価; 細胞培養試験; チラン; パックセメンテーション; 等温等圧法; 骨形成能; アパタイト形成; 擬似体液

Calcium phosphate reaction layers were fabricated on titanium by pack cementation process, isobaric-isothermal process and their combination process to improve the bonecompatibility of titanium. The phase of the reaction layer was hydroxyapatite (HAp) and Ca-P-O-Ti graded layer, and its thickness was several μm. The reaction layer showed high bonding strength to the substrate and high ALP activity by the cell culture test. These results suggested that the new process effectively improved the bone compatibility of titanium.

为了改善钛的骨相容性，采用包埋法、等压等温法及其组合法在钛表面制备磷酸钙反应层。反应层的物相为羟基磷灰石（HAp）和Ca-P-O-Ti梯度层，厚度为几μm。细胞培养试验表明，反应层与基质结合强度高，碱性磷酸酶活性高。结果表明，新工艺有效地提高了钛的骨相容性。

项目成果

ドライプロセスを利用したチタンの骨適合化表面処理

采用干法工艺进行骨相容性钛表面处理

• 发表时间: 2011
• 作者: K. Ueda;Y. Kawasaki;T. Narushima;T. Goto;J. Kurihara;H. Nakagawa;H. Kawamura;上田恭介
• 通讯作者: 上田恭介

リン酸四カルシウム粉末を用いたパックセメンテーション法によるチタンの表面改質

磷酸四钙粉包埋法对钛表面改性

• 发表时间: 2010
• 作者: 成島尚之;上田恭介;須藤初
• 通讯作者: 須藤初

Bioceramics coating on titanium materials

钛材料上的生物陶瓷涂层

• 发表时间: 2010
• 作者: 成島尚之;上田恭介;須藤初;K. Ueda
• 通讯作者: K. Ueda

Calcium phosphate films with/without heat treatments fabricated using RF magnetron sputtering

使用射频磁控溅射制造的经过/不经过热处理的磷酸钙薄膜

• 发表时间: 2009
• 期刊: J. Biomech. Sci. Eng.
• 作者: K. Ueda;Y. Kawasaki;T. Narushima;T. Goto;J. Kurihara;H. Nakagawa;H. Kawamura
• 通讯作者: H. Kawamura

リン酸四カルシウム粉末を用いたパックセメンテーション法によるチタンの骨適合化表面改質

磷酸四钙粉末包埋法对钛骨相容性表面进行改性

• 发表时间: 2009
• 作者: 上田恭介;須藤初;中家香織;成島尚之
• 通讯作者: 成島尚之