Isotropic thick film magnets prepared by using high purification and texture control

采用高纯度和织构控制制备的各向同性厚膜磁体

• 批准号: 22360129
• 负责人: NAKANO Masaki
• 金额: $ 12.15万
• 依托单位: Nagasaki University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (B)
• 财政年份: 2010
• 资助国家: 日本
• 起止时间: 2010-04-01 至 2014-03-31
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-22360129/
• 关键词: 電気・電子材料; 厚膜磁石; ナノコンポジット磁石; PLD; YAGレーザ; 保磁力; 残留磁化; 微細化; PLD法; Nd-Fe-B系磁石; デバイス応用; 電気電子材料; 多極着磁; ミリサイズモータ; 低速高トルク; 高速成膜; 等方性磁石膜; 添加物; 高トルク小型モータ; 高成膜速度

In order to upgrade the torque of the small motor further, increase in the remenence value of the isotropic films is indispensable. In this study, therefore, we prepared nano-composite Nd-Fe-B/Alpha-Fe thick-films with dispersion structure by using a PLD (Pulsed Laser Deposition) method. In particular, we focused on the reduction in size and/or numbers of droplets by controlling the focus of laser beam. Resultantly, we succeeded in obtaining a Nd-Fe-B nano-composite thick film magnet with remanence, coercivity and (BH)max values of approximately 1.0 T, 400 kA/m and 100 kJ/m3, respectively.

为了进一步提高小电机的转矩，必须提高各向同性薄膜的剩磁值。因此，本研究采用脉冲激光沉积（PLD）法制备了具有弥散结构的Nd-Fe-B/α-Fe纳米复合厚膜。特别地，我们专注于通过控制激光束的焦点来减小液滴的尺寸和/或数量。结果表明，我们成功地制备出了剩磁、矫顽力和（BH）max分别约为1.0 T、400 kA/m和100 kJ/m3的Nd-Fe-B纳米复合厚膜磁体。

项目成果

Numerical Study of Enhanced Coercivity of a Magnetically Hard Grain with Thin Surface Layers Due to Antiferromagnetic Coupling

反铁磁耦合导致薄表面层硬磁晶粒增强矫顽力的数值研究

• DOI: 10.1109/tmag.2012.2201707
• 发表时间: 2012
• 期刊: IEEE Trans. Magn
• 作者: H. Fukunaga;Y. Yokoi;M. Nakano;and T. Yanai
• 通讯作者: and T. Yanai

添加物を施した等方性厚膜磁石

含有添加剂的各向同性厚膜磁体

• 发表时间: 2010
• 作者: Takafumi Fukushima;Eiji Iwata;Yuki Ohara;Mariappan Murugesan;Jichoel Bea;Kangwook Lee;Tetsu Tanaka;Mitsumasa Koyanagi;松浦祐司;中野正基
• 通讯作者: 中野正基

Enhancement in magnetic torque of cylindrical micro rotor by usage of directly consolidated-Fe/Pr2Fe14B-based nanocomposite thick-films

利用直接固结Fe/Pr2Fe14B基纳米复合材料厚膜增强圆柱形微型转子的磁扭矩

• DOI: 10.1063/1.3553934
• 发表时间: 2011
• 期刊: Journal of Applied Physics
• 影响因子: 3.2
• 作者: F.Yamashita;S.Nishimura;O.Kobayashi;M.Itoh;M.Nakano;H.Fukunaga;K.Ishiyama
• 通讯作者: K.Ishiyama

Effect of laser beam parameters on magnetic properties of Nd-Fe-B thick-film magnets fabricated by pulsed laser deposition

激光束参数对脉冲激光沉积Nd-Fe-B厚膜磁体磁性能的影响

• DOI: 10.1063/1.3566080
• 发表时间: 2011
• 期刊: Journal of Applied Physics
• 影响因子: 3.2
• 作者: H.Fukunaga;T.Kamikawatoko;M.Nakano;T.Yanai;F.Yamashita
• 通讯作者: F.Yamashita

PLD法で作製した分散型Nd-Fe-B系ナノコンポジット厚膜磁石の磁気特性

PLD法制备分散Nd-Fe-B纳米复合厚膜磁体的磁性能

• 发表时间: 2012
• 作者: 林家弘;内山翔太;丸山隆浩;成塚重弥;Tomoaki Tsutsumi;本村浩介
• 通讯作者: 本村浩介