Control of cation distribution in spinel type iron oxide particles

尖晶石型氧化铁颗粒中阳离子分布的控制

• 批准号: 23360276
• 负责人: WASEDA Yoshio
• 金额: $ 12.23万
• 依托单位: Tohoku University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (B)
• 财政年份: 2011
• 资助国家: 日本
• 起止时间: 2011-04-01 至 2014-03-31
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-23360276/
• 关键词: 金属物性; 解析・評価; 放射線、X線、粒子線; 酸化鉄; 超常磁性; X線吸収分光; 放射線・X線・粒子線

The porous particles of maghemite were prepared from iron phosphate particles by a novel method using alkaline solution, and then these were immersed in a solution containing Co. The Co adsorbed porous particles of maghemite showed superparamagnetic behavior. The superparamagnetic blocking temperature of these particles was increased by the annealing. In addition, the results of X-ray absorption spectroscopy measurements showed that the local structure around Co in the Co adsorbed porous particles after annealing is very similar to that of CoFe2O4. Consequently, Co in the Co adsorbed porous particles after annealing probably locates at the cation vacancy site of maghemite.

采用一种新的方法，以磷酸铁为原料，在碱性溶液中制备磁赤铁矿多孔颗粒，然后将其浸泡在含Co溶液中，吸附Co的磁赤铁矿多孔颗粒表现出超顺磁性。这些粒子的超顺磁性阻断温度的提高，通过退火。此外，X射线吸收光谱测量的结果表明，在Co吸附的多孔粒子退火后的Co周围的局部结构是非常相似的CoFe2O4。因此，钴吸附多孔颗粒退火后的钴可能位于磁赤铁矿的阳离子空位位。

项目成果

準安定水酸化鉄の水溶液中酸化過程のその場X線吸収分光

亚稳态氢氧化铁在水溶液中氧化过程的原位X射线吸收光谱

• 发表时间: 2012
• 作者: 藤枝俊;吉野絢;篠田弘造;鈴木茂
• 通讯作者: 鈴木茂

液相処理による多孔質酸化鉄粒子の合成およびその特性

液相处理法制备多孔氧化铁颗粒及其性能

• 发表时间: 2012
• 作者: 福岡誠之;藤枝 俊;篠田弘造;鈴木 茂;早稲田嘉夫
• 通讯作者: 早稲田嘉夫

Co を吸着させた多孔質鉄酸化物の熱処理による局所構造変化

吸附Co的多孔氧化铁热处理引起的局部结构变化

• 发表时间: 2012
• 作者: 藤枝 俊;福岡誠之;篠田弘造;鈴木 茂;早稲田嘉夫
• 通讯作者: 早稲田嘉夫

液相合成多孔質酸化鉄粒子の構造および特性評価

液相合成多孔氧化铁颗粒的结构与表征

• 发表时间: 2013
• 作者: 篠田弘造;福岡誠之;藤枝俊;鈴木茂;早稲田嘉夫
• 通讯作者: 早稲田嘉夫

液相法により作製した多孔質酸化鉄粒子へのCo吸着およびその磁気特性

液相法制备的多孔氧化铁颗粒的Co吸附及其磁性能

• 发表时间: 2012
• 作者: 福岡誠之;藤枝俊;篠田弘造;鈴木茂;早稲田嘉夫
• 通讯作者: 早稲田嘉夫