Life Evaluation of Heat Resistant Steels with a Tempered Martensite Structure

回火马氏体组织耐热钢的寿命评价

• 批准号: 23360296
• 负责人: MARUYAMA Kouichi
• 金额: $ 12.4万
• 依托单位: Tohoku University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (B)
• 财政年份: 2011
• 资助国家: 日本
• 起止时间: 2011-04-01 至 2014-03-31
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-23360296/
• 关键词: 耐熱材料; 高クロム鋼; クリープ変形; クリープ破壊; 組織劣化; 損傷; 寿命評価; 長寿命化

Long-term creep life is estimated by time-temperature-parameter (TTP) methods. Such TTP methods overestimate creep life of creep strength enhanced ferritic (CSEF) steels. Decrease in activation energy Q for creep life in long-term creep of the steel is shown to be the cause of the overestimation. Creep life data of CSEF steel are divided into several data sets so that Q is unique in each divided data set, and then analyzed by a TTP method for creep life estimation. It has been proved that this multi-region analysis can properly estimate long-term creep lives. In creep of CSEF steels, recovery process of dislocation substructure is different between short-term and lon-term creep. This change in damage processes is the major cause of the decrease in Q value in long term-creep.

长期蠕变寿命估计的时间-温度-参数（TTP）的方法。这种TTP方法高估了蠕变强度增强铁素体（CSEF）钢的蠕变寿命。在长期蠕变的钢的蠕变寿命的激活能Q的降低被证明是高估的原因。将CSEF钢的蠕变寿命数据划分为若干个数据集，使每个数据集的Q值唯一，然后用TTP方法对数据集进行分析，估算蠕变寿命。实践证明，这种多区域分析方法可以正确地估计长期蠕变寿命。CSEF钢在蠕变过程中，短期和长期蠕变时位错亚结构的恢复过程不同。这种损伤过程的变化是长期蠕变Q值下降的主要原因。

项目成果

高Crフェライト鋼のクリープ損傷プロセスとその高温長時間使用による遷移

高铬铁素体钢高温长期使用的蠕变损伤过程及其转变

• 发表时间: 2013
• 作者: Hideki Arai;Ryosuke Yamauchi;Takanori Kiguchi;Koji Koyama;Keisuke Kobayashi;Toshimasa Suzuki;Takao Sasagawa;Yushi Kato;Nobuo Tsuchimine;Susumu Kobayashi;Masahiko Mitsuhashi;Satoru Kaneko;Mamoru Yoshimoto;中村浩二，白石嵩人，堀田篤;丸山公一
• 通讯作者: 丸山公一

Prediction of Long-Term Creep Rupture Life of Grade 122 Steel by Multiregion Analysis

• DOI: 10.1115/1.4028203
• 发表时间: 2015-04
• 期刊: Journal of Pressure Vessel Technology-transactions of The Asme
• 影响因子: 1
• 作者: K. Maruyama;J. Nakamura;K. Yoshimi

Strain-induced coarsening of nanoscale precipitates in strength enhanced high Cr ferritic steels

• DOI: 10.1016/j.msea.2011.10.105
• 发表时间: 2012-01-15
• 期刊: MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
• 影响因子: 6.4
• 作者: Armaki, Hassan Ghassemi;Chen, Ruiping;Igarashi, Masaaki
• 通讯作者: Igarashi, Masaaki

Development of Oxide Dispersion Strengthened Steels for High Temperature Nuclear Structural Applications

高温核结构应用氧化物弥散强化钢的开发

• DOI: 10.1007/978-0-85729-493-7_89
• 发表时间: 2011
• 期刊: Engineering Asset Management and Infrastructure Sustainability
• 作者: H.Zhu;T.Wei;R.Harrison;L.Edwards;K.Maruyama
• 通讯作者: K.Maruyama

高Cr フェライト鋼のクリープ損傷プロセスとその高温長時間使用による遷移

高铬铁素体钢高温长期使用的蠕变损伤过程及其转变

• 发表时间: 2013
• 作者: Ouchi;T.;Yamazaki;M.;Hotta;A.;丸山公一
• 通讯作者: 丸山公一